Adding rare earth into permeating agent has an obvious catalytic effect on vanadizing on steel surface, and the vanadizing rate can increase about 30%～40%. The case depth ( x ) of the samples which have undergone d...Adding rare earth into permeating agent has an obvious catalytic effect on vanadizing on steel surface, and the vanadizing rate can increase about 30%～40%. The case depth ( x ) of the samples which have undergone different periods of vanadizing time at 950 ℃ was measured. These depth values ( x ) and its corresponded time ( t ) were substituded into the experimental formula, i.e., x n=Kt (ln x=(1/n) ln K+(1/n) ln t ), and were processed by mono linear regression. It is found that x and t have the relationship of x 2=Kt . Addition of rare earth can promote reaction of the permeating agent, and increase vanadium potential of the agent. Rare earth, as a strong reductant, makes the oxide on the steel surface reduced, and thus activates the steel surface. Permeating of rare earth into steel and the VC layer intensifies the crystal fault density, and, together with its excellent chemical activation, makes carbon atoms diffuse easily. These functions of rare earth can decrease the diffusion activation energy of the carbon atoms, and therefore has catalytic effect on permeation.展开更多
The use of ＂bath salts＂ or other new psychoactive substances,otherwise known as ＂legal highs＂,is increasing.Illicit drug use during pregnancy is not uncommon.Nevertheless,literature reporting bath salts and their ...The use of ＂bath salts＂ or other new psychoactive substances,otherwise known as ＂legal highs＂,is increasing.Illicit drug use during pregnancy is not uncommon.Nevertheless,literature reporting bath salts and their effect on pregnancy is scant.Besides,there seems to be no literature about bath salts and conduct of general anesthesia.This case report describes a general anesthetic for the surgical delivery of an infant to a woman under the acute influence of bath salts and methamphetamines.展开更多
Vanadium pentoxide, borax, boron carbide and sodium fluoride were used to grow vanadium carbide coating on surface of Crl2 steel at 950℃ by TD process. The coating of vanadium carbide （VC） extended the serve-life p...Vanadium pentoxide, borax, boron carbide and sodium fluoride were used to grow vanadium carbide coating on surface of Crl2 steel at 950℃ by TD process. The coating of vanadium carbide （VC） extended the serve-life period of Crl2 steel as punching die. Kinetics of vanadium carbide coating growth was brought forward and verified by comparison of the mathematical model with the experimental results. The thickness of coating was illustrated by SEM. The chemical constituent of coating and remnants were tested by X-ray diffraction （XRD） and X-ray energy dispersive spectroscopy （EDS）. To increase the thickness, rare earth silicon powder （FeSiRe23） was added to the borax salt bath. The analysis of XRD revealed that FeSiRe23 increased the depth of vanadium car-bide coating as reducing agent and catalysis.展开更多
为满足跨江跨海大桥对高强度、高可靠性缆索的需求,通过优化高碳钢盘条成分设计,并采用盐浴替代铅浴处理,成功开发出∅7 mm 2100 MPa级桥梁缆索用热镀锌铝钢丝。所设计的QS92Si盘条主要化学成分:w(C)=0.93%~0.95%,w(Si)=1.0%~1.1%,w(Mn)=...为满足跨江跨海大桥对高强度、高可靠性缆索的需求,通过优化高碳钢盘条成分设计,并采用盐浴替代铅浴处理,成功开发出∅7 mm 2100 MPa级桥梁缆索用热镀锌铝钢丝。所设计的QS92Si盘条主要化学成分:w(C)=0.93%~0.95%,w(Si)=1.0%~1.1%,w(Mn)=0.5%~0.6%,w(Cr)=0.3%~0.4%。试制结果表明,经盐浴处理后,QS92Si盘条抗拉强度由1390~1460 MPa提高至1550~1650 MPa,断面收缩率由21%~28%提高至27%~33%;珠光体片层平均宽度由风冷态的90 nm细化至70 nm,满足制备∅7 mm 2100 MPa级热镀锌铝钢丝的原料要求。最终成品钢丝的平均抗拉强度为2160 MPa,平均断后伸长率为5.6%,平均扭转为19次,其余各项性能指标均符合标准要求。展开更多
文摘Adding rare earth into permeating agent has an obvious catalytic effect on vanadizing on steel surface, and the vanadizing rate can increase about 30%～40%. The case depth ( x ) of the samples which have undergone different periods of vanadizing time at 950 ℃ was measured. These depth values ( x ) and its corresponded time ( t ) were substituded into the experimental formula, i.e., x n=Kt (ln x=(1/n) ln K+(1/n) ln t ), and were processed by mono linear regression. It is found that x and t have the relationship of x 2=Kt . Addition of rare earth can promote reaction of the permeating agent, and increase vanadium potential of the agent. Rare earth, as a strong reductant, makes the oxide on the steel surface reduced, and thus activates the steel surface. Permeating of rare earth into steel and the VC layer intensifies the crystal fault density, and, together with its excellent chemical activation, makes carbon atoms diffuse easily. These functions of rare earth can decrease the diffusion activation energy of the carbon atoms, and therefore has catalytic effect on permeation.
文摘The use of ＂bath salts＂ or other new psychoactive substances,otherwise known as ＂legal highs＂,is increasing.Illicit drug use during pregnancy is not uncommon.Nevertheless,literature reporting bath salts and their effect on pregnancy is scant.Besides,there seems to be no literature about bath salts and conduct of general anesthesia.This case report describes a general anesthetic for the surgical delivery of an infant to a woman under the acute influence of bath salts and methamphetamines.
基金Funded by the National Natural Science Foundation of China (No.50675165)the National Key Technology R&D Program (No.2006BAF02A29)
文摘Vanadium pentoxide, borax, boron carbide and sodium fluoride were used to grow vanadium carbide coating on surface of Crl2 steel at 950℃ by TD process. The coating of vanadium carbide （VC） extended the serve-life period of Crl2 steel as punching die. Kinetics of vanadium carbide coating growth was brought forward and verified by comparison of the mathematical model with the experimental results. The thickness of coating was illustrated by SEM. The chemical constituent of coating and remnants were tested by X-ray diffraction （XRD） and X-ray energy dispersive spectroscopy （EDS）. To increase the thickness, rare earth silicon powder （FeSiRe23） was added to the borax salt bath. The analysis of XRD revealed that FeSiRe23 increased the depth of vanadium car-bide coating as reducing agent and catalysis.