摘要
利用气相平衡扩散法研制出掺镁不同组分的LiNbO3晶体 ,并对其极化特性进行了研究 .研究表明晶体的开关电场和自发极化不仅与晶体组分 [Li] [Nb]比有关而且与掺镁量有关 ,[Li] [Nb]比为 0 973掺入 2mol%MgO的近化学比LiNbO3晶体的开关电场仅为 1 8kV mm ,是同成分晶体的 1 12 ,且其极化结构的质量要远好于同成分LiNbO3晶体和近化学比LiNbO3晶体 .
LiNbO 3 crystals doped with different amount of MgO have been produced using vapor transport equilibration technique. The poling characteristics of the crystals with different MgO doping levels have been investigated. The switching field and the spontaneous polarization P s of the crystals were expressed as functions of crystal stoichiometry and Mg content. The switching field for the domain reversal in the near stoichiometric crystal with [Li]/[Nb]=0 973 doped with 2 0mol.% MgO was 1 8kV/mm. This is about one twelfth of the switching field for the congruent crystal, and the pattern of the periodic domain in the crystal is better than in the congruent and stoichiometric crystal.
出处
《物理学报》
SCIE
EI
CAS
CSCD
北大核心
2004年第1期156-159,共4页
Acta Physica Sinica
基金
国家自然科学基金 (批准号 :10 1740 40
90 10 10 2 2 )
天津市重点自然科学基金
天津市国际合作项目资助的课题~~