摘要
为了提高宽幅双零箔材的表面质量,通过制定合理的试验方案和拟定轧制工艺参数,反复现场对比试验,分析试验结果,最后确定了轧制宽幅双零铝箔的最佳生产工艺参数。实践证明,所制定的生产工艺合理,且轧制的宽幅双零箔材表面质量明显提高,满足了用户要求。
In order to improve the surface quality of double zero aluminum foil with wide width, the best rolling process parameters of double zero aluminum foil with wide width were determined through establishing the reasonable testing scheme and studying out rolling process parameters, contrast test repeatedly and analyzing of test results. The practice had proved that developed production process was reasonably, and rolled surface quality of double zero aluminum foil with wide width was improved obviously, and met the requirements of customers.
出处
《轻金属》
CSCD
北大核心
2015年第9期52-54,共3页
Light Metals
关键词
轧制
宽幅
铝箔
试验
分析
rolling
wide width
aluminum foil
analysis