摘要
利用固 -固相反应制得纳米氧化锌 ,经分散处理后对w(纳米氧化锌 ) =0 0 12 5 %～ 0 2 %的水溶胶在波长为 2 0 0～ 80 0nm的光区进行了透光率和吸光度分析。结果表明 :纳米氧化锌在 4 2 5～ 80 0nm光区有普通氧化锌所不具备的高度透明性 ,平均透过率最大的为 96 9% ,最小的为 5 5 3% ;在 2 0 0～ 4 2 4nm光区有很强的紫外光宽带吸收 ,w(纳米氧化锌 ) =0 0 1%时吸光度最大 ,超过 2 5 ,是同质量普通氧化锌的 13倍。考虑到纳米氧化锌对可见光的透明性和紫外光的遮蔽性 ,其质量分数在 0 0 5 %～ 0 1%较合适。
Nanometer zinc oxide was produced by solid solid phase reaction.After dispersed in water,the solution 〔 w (nanometer zinc oxide)= 0 0125%-0 2%〕 was analyzed by ultraviolet and visible spectrometry between 200 nm and 800 nm.The results show that nanometer zinc oxide solution is transparent at the range of 425nm-800 nm,the maximum average transmittance is 96 9%,and the minimum is 55 3%.Nanometer zinc oxide exhibits strong wide band absorption in ultraviolet zone of 200 nm-424 nm;when w (nanometer zinc oxide)=0 01%,the absorbance was larger than 2 5,which is thirteen times that of equivalent normal zinc oxide.For favorite transparency to visible light and shield to ultraviolet light ,the applicable mass ratio is 0 05%-0 1 %.
出处
《精细化工》
EI
CAS
CSCD
北大核心
2002年第2期93-94,111,共3页
Fine Chemicals
基金
湖南省自然科学基金资助项目 (99JJY2 0 71)
湖南省教育厅科研基金资助项目 (0 0C191)~~
关键词
纳米氧化锌
水溶胶
紫外--可见光
透明性
nanometer zinc oxide
ultraviolet and visible spectrum
transparency