摘要
以天然鳞片石墨为原料,采用Staudenmaier法先制备出石墨氧化物,再经饱和碳酸铵溶液浸渍后生成NH4+插层石墨氧化物.在微波照射下,NH4+分解生成的NH3与剥离的石墨烯氧化物反应原位合成出氮掺杂石墨烯.通过SEM、TEM、EDS、XRD、XPS和Raman测试手段对氮掺杂石墨烯进行了表征.结果表明,所合成的氮掺杂石墨烯呈透明绢丝状结构,每个石墨烯片含有2～5层石墨层;氮元素含量为1.56wt%,其中N元素是以pyridinc N、pyrrolic N和graphitic N形式掺入石墨层网格中.
Graphite oxide was synthesized with Staudenmaier method using natural flake graphite as carbon source.After graphite oxide was impregnated into ammonium carbonate saturated solution,NH4＋ intercalated graphite oxide was given.Rapid thermal exfoliation and reduction of NH4＋ intercalated graphite oxide to graphene was achieved as well as the nitrogen-doping of graphene under the condition of microwave irradiation.SEM,TEM,EDS,XRD,XPS and Raman were performed to characterize the synthesized nitrogen-doping of graphene.The synthesized nitrogen-doped graphene was transparent and wrinkled with 2 5 graphite layers.The nitrogen content of as-prepared nitrogen-doped graphene was 1.56wt%,corresponding to pyridinc N,pyrrolic N and graphitic N incorporated into the graphitic network.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2012年第2期146-150,共5页
Journal of Inorganic Materials
基金
国家自然科学基金(20806024
50672025
5073003
51002051)
中央高校基本科研业务费专项基金(WA1014016)
国家863重点项目(2008AA062302)~~
关键词
石墨烯
氮掺杂
微波辐照气相法
graphene
nitrogen-doped
microwave irradiation