摘要
用雾化沉积工艺方法制备了Ａｌ８Ｐｂ４Ｓｉ１．５Ｓｎ１Ｃｕ合金板坯，并与铝箔一起进行轧制复合试验。金相及ＳＥＭ观察表明：在沉积态ＡｌＰｂ合金中，富铅相颗粒细小且分布均匀，不存在宏观偏析；经过复合轧制后，铝箔与沉积态ＡｌＰｂ合金的基体之间不存在明显界面，形成了良好的界面结合。
Plate blanks of Al8Pb4Si1.5Sn1Cu alloy were made by spray deposition process, and cladding rolling of this kind of plate with Al foil was experimented. The results of SEM and microstructure analysis show that higher Pbrich was refined and distributed evenly in asdeposited AlPb alloy; there is no obvious interface between Al foil and asdeposited AlPb alloy matrix after cladding rolling.
出处
《稀有金属》
EI
CAS
CSCD
北大核心
1999年第3期233-235,共3页
Chinese Journal of Rare Metals