蓝宝石邻晶面衬底MBE生长GaN薄膜的瞬态光电导弛豫特性研究 被引量:2

Instantaneous relaxation of photoconductivity in GaN film grown on vicinal sapphire substrate by MBE
原文传递
导出
摘要 在实验优化MBE工艺条件的基础上,采用蓝宝石(0001)邻晶面衬底制备出了具有较高质量的GaN薄膜.XRD分析表明邻晶面衬底生长的GaN薄膜晶体结构质量明显提高,AFM表征结果显示邻晶面生长的样品表面形貌显著改善.蓝宝石衬底GaN薄膜的瞬态光电导弛豫特性对比实验研究发现,常规衬底生长的GaN薄膜光电导弛豫特性出现双分子复合、单分子复合和弛豫振荡三个过程,持续时间分别为0.91,7.7和35.5ms;蓝宝石邻晶面衬底生长的GaN薄膜光电导弛豫过程主要是双分子复合和单分子复合过程,持续时间分别为0.78和14ms.理论分析表明MBE生长GaN薄膜的持续光电导效应主要起源于本生位错缺陷引发的深能级. By optimizing the technique and conditions experimentally, we have grown GaN film on vicinal sapphire (0001) substrates by radio frequency plasma-assisted molecular beam epitaxy ( MBE). It was found that the films grown on vicinal sapphire (0001) substrates have better quality than that grown on conventional substrate, as shovn by XRD and AFM characterization. Through investigation of the instantaneous relaxation behaviors of photoconductivity in GaN films grown on vicinal and common sapphire substrates, three stages of carrier recombination in the conventional MBE GaN film were discovered. The stages consist of bimolecular, monomolecular and persistent recombination phases in which the relaxation times are 0.91, 7.7 and 35.5ms, respectively. In comparison, only bimolecular and monomolecular recombination processes of photo-generated carriers were found inthe GaN film grown on vicinal sapphire (0001) substrate, the relaxation time was measured to be 0.78 and 14 ms, respectively. Theoretical considerations directly show that the persistent conductivity mainly originates from the native dislocation defects in GaN film grown by MBE.
出处 《物理学报》 SCIE EI CAS CSCD 北大核心 2007年第7期4218-4223,共6页 Acta Physica Sinica
基金 国家自然科学基金(批准号:10474078)资助的课题.~~
关键词 邻晶面蓝宝石衬底 GAN薄膜 瞬态光电导 弛豫特性 vicinal sapphire substrate, GaN film, instantaneous photoconductivity, relaxation
  • 相关文献

参考文献12

  • 1Razeghi M,Rogaiski A 1996 J.Appl.Phys.79 7433
  • 2Munoz E,Monroy E,Pau J L,Calle F,Omnes F,Gibart P 2001 J.Phys.:Condens.Matter 13 7115
  • 3He Z,Kang Y,Tang Y W,Li X,Fang J X 2006 Chin.Phys.15 1325
  • 4Carrano J C,Li T,Grudowski P A,Eiting C J,Dupuis R D,Campbell J C 1998 J.Appl.Phys.83 6148
  • 5Hirseh M T,Wolk J A,Walukiewicz W,Hailer E E 1997 Appl.Phys.Lett.71 1098
  • 6Li J Z,Lin J Y,Jiang H X,Khan M A 1998 Appl.Phys.Lett.72 2868
  • 7Parish G.,Keller S,Ibbetsan J P,Marchand H,Fini P T,Fleiseber S B,Denbaars S P,Mishra U K,Tarsa E J 1999 Appl.Phys.Lett.75 247
  • 8Sben X Q,Shimizu M,Yamamoto T,Honda Y,Okumura H 2005 Journal of Crystal Growth 278 378
  • 9Binet F,Duboz J Y,Rosencber E,Schoiz F,Harle V 1996 Appl.Phys.Lett.69 1202
  • 10Jiang H X and Lin J Y 2000 M.O.Manasreh(Ed) Elsevier Science B.V.170

二级参考文献7

共引文献13

同被引文献16

  • 1段理,林碧霞,傅竹西,蔡俊江,张子俞.ZnO/p-Si异质结的光电转换特性[J].Journal of Semiconductors,2005,26(10):1963-1967. 被引量:6
  • 2Baik D C., Cho S M 1999 Thin Solid Films 354 227
  • 3Fu Z X, Lin B X, Liao G H 1999 Chin. Phys. Lett. 16 753
  • 4Kobayashi H, Mori H, Ishida T, Nakato Y 1995 J. Appl. Phys. 77 1301
  • 5Song D Y, Aberle A G, Xia J 2002 Appl. Surf. Sci. 195 291
  • 6Shukri Z A, Yip L S, Qiu C X, Shih I, Champness C H 1995 Sol. Energy Mater. Sol. Cells 37 395
  • 7Kessler J, Ruekh M, Velthaus K O, Schock H W 1993 Appl. Phys. Lett. 62 597
  • 8Jasenek A, Rau U, Weinert K, Kotschau I M, Hanna G, Voorwinden G, Powalla M, Schock H W, Werner J H 2001 Thin Solid Films 387 228
  • 9Mfidha S, Basak D 2007 J. Appl. Phys. 101 083102-1
  • 10Jeong I S, Kim J H, Park H H, Im S 2004 Thin solidfilms 447-448 111

引证文献2

二级引证文献5

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部