摘要
在含有0.2mol·L^-1苯胺的0.5 mol·L^1H2SO4溶液中,以扫描速度50mV·s^-1,扫描电位为-0.1～0.9V,采用循环伏安法（CV）,在金属Ti基体上,通过控制扫描方式分别得到了颗粒状、纤维状及管-片状的苯胺聚合产物,分析了形成不同形貌聚苯胺的原因,并通过扫描电子显微镜（SEM）、循环伏安法和电化学阻抗谱（EIS）对不同形貌聚苯胺的结构和性能进行了表征.结果表明,不同形貌聚苯胺的形成是由于聚苯胺的成核及生长模式不同,而无论何种形貌的聚苯胺膜都具有很大的比表面积和良好的导电性能,其中,管-片状聚苯胺的膜层阻抗最小,导电性能最好.
Polyaniline films on Ti-based metal substmtes with granular, fibrillar and tube-slice surface morphology were prepared in a 0. 2 mol·L^-1 aniline solution in 0. 5 mol·L^-1 sulfuric acid by using the cyclic vohammetry method with scanning valtages in the range of - 0.1 V ～ 0.9 V at a scanning rate of 50 mV · s^-1. The electrochemical properties and structure of polyaniline film electrodes were characterized by SEM, cyclic vohammetry （CV） and electrochemical impedance spectra （EIS）. The result show that the different surface morphology of polyaniline films has different nucleation and growth mechanism, and polyaniline on Ti-based metal has prodigious surface area and good electrical conductivity. The tube-slice polyaniline has the least film impedance and the best electrical conductivity.
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2007年第6期536-540,共5页
Acta Polymerica Sinica
基金
国家自然科学基金(基金号20476001)
安徽省教育厅自然基金项目(基金号KJ2007B386ZC)
安徽科技学院自然科学课题(课题号2006YZ015)资助项目
关键词
聚苯胺
电化学聚合
循环伏安
电化学阻抗谱
Polyaniline, Electrochemical polymerization, Cyclic vohammetry （ CV）, Electrochemical impedance spectra （EIS）