The solidification and corrosion behavior of the Ti/B added Zn-Al-Mg alloys were experimentally investigated by means of microstructure characterization and electrochemical test.The basic calculations were carried out...The solidification and corrosion behavior of the Ti/B added Zn-Al-Mg alloys were experimentally investigated by means of microstructure characterization and electrochemical test.The basic calculations were carried out to predict the characteristics of the Ti-added Zn-Al-Mg alloys.The Zn-Al-Mg ingots with minor doping of Ti/B were prepared and solidified under different cooling rate,including air cooling,water quenching and furnace cooling.The scanning electron microscopy(SEM)and the X-ray diffraction method(XRD)were used to determine the microstructures and phase types of the alloy samples.It could be discovered that trace TiAl3 particles were dispersed in the Ti/B added alloy samples which provide the heterogeneous nucleation sites to refine the size of the dendrites and the eutectic microstructures.More fined microstructures with the addition of both Ti and B were obtained compared with those with the merely addition of Ti,and the water cooled alloys presented the finest microstructures due to the fastest cooling rate.It could also be noticed that with the increasing solidification rate,the percentage of the MgZn_(2) phase turned out to be higher because of the Mg_(2)Zn_(11)↔MgZn_(2) transition,which is in consistent with the results in the actual hot-dip galvanizing process.Electrochemical experiments in the previous work included methods the of the Tafel polarization test and the electrochemical impedance spectroscopy test(EIS).Results show that the quenched Zn-Al-Mg alloy with the addition of both Ti and B takes on best corrosion resistance.Consequently,the addition of certain amount of Ti/B elements and the appropriate elevation of the cooling rate will be the practicable approaches to optimize the microstructure and the corrosion resistance of the Zn-Al-Mg coatings in the actual galvanizing process.展开更多
Al-Cu-Mn-Mg合金因其优异的综合性能,被广泛应用于航空航天和轨道交通等领域。然而,该合金在铸造过程中容易出现热裂缺陷,严重影响铸件的质量和可靠性。因此,提高合金的晶粒细化效果,对于改善合金的铸造性能具有重要意义。Al-Ti-B细化...Al-Cu-Mn-Mg合金因其优异的综合性能,被广泛应用于航空航天和轨道交通等领域。然而,该合金在铸造过程中容易出现热裂缺陷,严重影响铸件的质量和可靠性。因此,提高合金的晶粒细化效果,对于改善合金的铸造性能具有重要意义。Al-Ti-B细化剂是铝合金铸造中最常用的晶粒细化剂,但不同Ti/B质量比的Al-Ti-B细化剂对晶粒细化效果及热裂机制尚未系统研究。采用X射线衍射仪(XRD)、光学显微镜(OM)、扫描电镜(SEM)和CRC(constrained rod cast)金属型约束热裂棒模具等,分析了不同Ti/B质量比的Al-Ti-B细化剂对铸造Al-Cu-Mn-Mg合金微观组织和热裂倾向性的影响。实验结果表明,4种Ti/B比的Al-Ti-B细化剂中Al_3Ti和TiB_2相的含量存在显著差异。在B含量均为0.3%(质量分数)的条件下,添加Al-3Ti-1B、Al-4Ti-1B、Al-5Ti-1B和Al-5Ti-2B的Al-5Cu-0.7Mn-0.55Mg合金的平均晶粒尺寸分别为162.07、113.73、107.81和88.00μm,对应的热裂纹倾向性指数依次为112、136、96和24。微观机制分析表明,Ti B_(2)相的含量对晶粒细化效果和热裂倾向性具有显著影响。特别是Al-5Ti-2B细化剂,在晶粒细化的同时,显著降低了合金的热裂倾向性,展现出优异的性能。展开更多
l Ti B中间合金是一种高效实用的铝合金晶粒细化剂。本文指出了Al Ti B的潜力、不足和发展趋势。概述了Al Ti B结构遗传的化学和物理基础及影响因素 ,Al Ti B细化行为的结构遗传效应 ,TiAl3 在铝熔体结构遗传中的动力学行为 ,α Al的形...l Ti B中间合金是一种高效实用的铝合金晶粒细化剂。本文指出了Al Ti B的潜力、不足和发展趋势。概述了Al Ti B结构遗传的化学和物理基础及影响因素 ,Al Ti B细化行为的结构遗传效应 ,TiAl3 在铝熔体结构遗传中的动力学行为 ,α Al的形核机制。提出了新的Al Ti B制备技术和微细化处理工艺。认为随着Al Ti B质量的不断改进 ,尤其是高效洁净稳定型Al Ti B的出现 ,Al Ti展开更多
A series of Al-Ti-B master alloys were prepared by different preparation routes,and the TiB2 particles in the master alloys were extracted and analyzed.It is found that the forming process has significant influence on...A series of Al-Ti-B master alloys were prepared by different preparation routes,and the TiB2 particles in the master alloys were extracted and analyzed.It is found that the forming process has significant influence on the three-dimensional morphology of TiB2 particles.Different preparation routes result in different reaction forms,which accounts for the morphology variation of TiB2 particles.When the Al-Ti-B master alloy is prepared using ＂halide salt＂ route,TiB2 particles exhibit hexagonal platelet morphology and are independent with each other.In addition,the reaction temperature almost does not have influence on the morphology of TiB2 particles.However,TiB2 particles exhibit different morphologies at different reaction temperatures when the master alloys are prepared with Al-3B and Ti sponge.When the master alloy is prepared at 850 ℃,a kind of TiB2 particle agglomeration forms with a size larger than 5 μm.The TiB2 particles change to layered stacking morphology even dendritic morphology with the reaction temperature reaching up to 1200 ℃.展开更多
基金Funded by the Provincial Key Research and Development Program of Hebei(No.20311004D)the Foundation of Shougang Research Institute of Technology(No.2020RZ06-031)。
文摘The solidification and corrosion behavior of the Ti/B added Zn-Al-Mg alloys were experimentally investigated by means of microstructure characterization and electrochemical test.The basic calculations were carried out to predict the characteristics of the Ti-added Zn-Al-Mg alloys.The Zn-Al-Mg ingots with minor doping of Ti/B were prepared and solidified under different cooling rate,including air cooling,water quenching and furnace cooling.The scanning electron microscopy(SEM)and the X-ray diffraction method(XRD)were used to determine the microstructures and phase types of the alloy samples.It could be discovered that trace TiAl3 particles were dispersed in the Ti/B added alloy samples which provide the heterogeneous nucleation sites to refine the size of the dendrites and the eutectic microstructures.More fined microstructures with the addition of both Ti and B were obtained compared with those with the merely addition of Ti,and the water cooled alloys presented the finest microstructures due to the fastest cooling rate.It could also be noticed that with the increasing solidification rate,the percentage of the MgZn_(2) phase turned out to be higher because of the Mg_(2)Zn_(11)↔MgZn_(2) transition,which is in consistent with the results in the actual hot-dip galvanizing process.Electrochemical experiments in the previous work included methods the of the Tafel polarization test and the electrochemical impedance spectroscopy test(EIS).Results show that the quenched Zn-Al-Mg alloy with the addition of both Ti and B takes on best corrosion resistance.Consequently,the addition of certain amount of Ti/B elements and the appropriate elevation of the cooling rate will be the practicable approaches to optimize the microstructure and the corrosion resistance of the Zn-Al-Mg coatings in the actual galvanizing process.
文摘Al-Cu-Mn-Mg合金因其优异的综合性能,被广泛应用于航空航天和轨道交通等领域。然而,该合金在铸造过程中容易出现热裂缺陷,严重影响铸件的质量和可靠性。因此,提高合金的晶粒细化效果,对于改善合金的铸造性能具有重要意义。Al-Ti-B细化剂是铝合金铸造中最常用的晶粒细化剂,但不同Ti/B质量比的Al-Ti-B细化剂对晶粒细化效果及热裂机制尚未系统研究。采用X射线衍射仪(XRD)、光学显微镜(OM)、扫描电镜(SEM)和CRC(constrained rod cast)金属型约束热裂棒模具等,分析了不同Ti/B质量比的Al-Ti-B细化剂对铸造Al-Cu-Mn-Mg合金微观组织和热裂倾向性的影响。实验结果表明,4种Ti/B比的Al-Ti-B细化剂中Al_3Ti和TiB_2相的含量存在显著差异。在B含量均为0.3%(质量分数)的条件下,添加Al-3Ti-1B、Al-4Ti-1B、Al-5Ti-1B和Al-5Ti-2B的Al-5Cu-0.7Mn-0.55Mg合金的平均晶粒尺寸分别为162.07、113.73、107.81和88.00μm,对应的热裂纹倾向性指数依次为112、136、96和24。微观机制分析表明,Ti B_(2)相的含量对晶粒细化效果和热裂倾向性具有显著影响。特别是Al-5Ti-2B细化剂,在晶粒细化的同时,显著降低了合金的热裂倾向性,展现出优异的性能。
文摘l Ti B中间合金是一种高效实用的铝合金晶粒细化剂。本文指出了Al Ti B的潜力、不足和发展趋势。概述了Al Ti B结构遗传的化学和物理基础及影响因素 ,Al Ti B细化行为的结构遗传效应 ,TiAl3 在铝熔体结构遗传中的动力学行为 ,α Al的形核机制。提出了新的Al Ti B制备技术和微细化处理工艺。认为随着Al Ti B质量的不断改进 ,尤其是高效洁净稳定型Al Ti B的出现 ,Al Ti
基金Project(50625101) supported by the National Science Fund for Distinguished Young Scholars of ChinaProject supported by Graduate Independent Innovation Foundation of Shandong University(GIIFSDU),ChinaProject(51071097) supported by the National Natural Science Foundation of China
文摘A series of Al-Ti-B master alloys were prepared by different preparation routes,and the TiB2 particles in the master alloys were extracted and analyzed.It is found that the forming process has significant influence on the three-dimensional morphology of TiB2 particles.Different preparation routes result in different reaction forms,which accounts for the morphology variation of TiB2 particles.When the Al-Ti-B master alloy is prepared using ＂halide salt＂ route,TiB2 particles exhibit hexagonal platelet morphology and are independent with each other.In addition,the reaction temperature almost does not have influence on the morphology of TiB2 particles.However,TiB2 particles exhibit different morphologies at different reaction temperatures when the master alloys are prepared with Al-3B and Ti sponge.When the master alloy is prepared at 850 ℃,a kind of TiB2 particle agglomeration forms with a size larger than 5 μm.The TiB2 particles change to layered stacking morphology even dendritic morphology with the reaction temperature reaching up to 1200 ℃.