GaAs-based nanomaterials are essential for near-infrared nano-photoelectronic devices due to their exceptional optoelectronic properties.However,as the dimensions of GaAs materials decrease,the development of GaAs nan...GaAs-based nanomaterials are essential for near-infrared nano-photoelectronic devices due to their exceptional optoelectronic properties.However,as the dimensions of GaAs materials decrease,the development of GaAs nanowires(NWs)is hindered by type-Ⅱquantum well structures arising from the mixture of zinc blende(ZB)and wurtzite(WZ)phases and surface defects due to the large surface-to-volume ratio.Achieving GaAs-based NWs with high emission efficiency has become a key research focus.In this study,pre-etched silicon substrates were combined with GaAs/AlGaAs core-shell heterostructure to achieve GaAs-based NWs with good perpendicularity,excellent crystal structures,and high emission efficiency by leveraging the shadowing effect and surface passivation.The primary evidence for this includes the prominent free-exciton emission in the variable-temperature spectra and the low thermal activation energy indicated by the variable-power spectra.The findings of this study suggest that the growth method described herein can be employed to enhance the crystal structure and optical properties of otherⅢ-Ⅴlow-dimensional materials,potentially paving the way for future NW devices.展开更多
量子阱红外探测器(Quantum well infrared photodetector,QWIP)已经经历了20多年的深入研究,各种QWIP器件,包括量子阱红外探测器焦平面阵列(FPA)的研制也已经相当成熟。但是在国内,受制于整体工业水平,QWIP焦平面阵列器件的研制仍然处...量子阱红外探测器(Quantum well infrared photodetector,QWIP)已经经历了20多年的深入研究,各种QWIP器件,包括量子阱红外探测器焦平面阵列(FPA)的研制也已经相当成熟。但是在国内,受制于整体工业水平,QWIP焦平面阵列器件的研制仍然处于起步阶段。研制了基于GaAs/AlxGa1-xAs材料、峰值响应波长为9.9μm的长波320×256 n型QWIP焦平面阵列器件,其像元中心距25μm,光敏元面积为22μm×22μm。GaAs衬底减薄后的QWIP焦平面阵列,与Si基CMOS读出电路(ROIC)通过铟柱倒焊互连,并且在65 K工作温度下进行了室温环境目标成像。该焦平面器件的规模和成像质量相比之前国内报道的结果都有较大提高。焦平面平均峰值探测率达1.5×1010cm.Hz1/2/W。展开更多
We design and fabricate a 128 × 128 AlGaAs/GaAs quantum well infrared photodetector focal plane array （FPA）. The device is achieved by metal organic chemical vapor deposition and GaAs integrated circuit process...We design and fabricate a 128 × 128 AlGaAs/GaAs quantum well infrared photodetector focal plane array （FPA）. The device is achieved by metal organic chemical vapor deposition and GaAs integrated circuit processing technology. A test structure of the photodetector with a mesa size of 300μm × 300μm is also made in order to obtain the device parameters. The measured dark current density at 77K is 1.5 × 10^-3A/cm^2 with a bias voltage of 2V. The peak of the responsivity spectrum is at 8.4μm,with a cutoff wavelength of 9μm. The blackbody detectivity is shown to be 3.95 × 10^8 （cm · Hz^1/2）/W. The final FPA is flip-chip bonded on a CMOS read-out integrated circuit. The infrared thermal images of some targets at room temperature background are successfully demonstrated at 80K operating temperature with a ratio of dead pixels of less than 1%.展开更多
利用各向异性的湿法刻蚀和侧墙隔离技术实现了发射极金属和基极金属的自对准 ,采用该自对准技术成功地研制出了自对准结构的 Al Ga As/ Ga As异质结双极晶体管 ,器件直流电流增益大于 2 0 ,电流增益截止频率 f T 大于30 GHz,最高振荡频...利用各向异性的湿法刻蚀和侧墙隔离技术实现了发射极金属和基极金属的自对准 ,采用该自对准技术成功地研制出了自对准结构的 Al Ga As/ Ga As异质结双极晶体管 ,器件直流电流增益大于 2 0 ,电流增益截止频率 f T 大于30 GHz,最高振荡频率 fmax大于 5 0 GHz,连续波功率测量表明 :在 1d B增益压缩时 ,单指 HBT可以提供 10 0 m W输出功率 ,对应的功率密度为 6 .6 7W/ m m,功率饱和时最大输出功率 112 m W,对应功率密度为 7.48W/ m m,功率附加效率为 6 7%展开更多
文摘GaAs-based nanomaterials are essential for near-infrared nano-photoelectronic devices due to their exceptional optoelectronic properties.However,as the dimensions of GaAs materials decrease,the development of GaAs nanowires(NWs)is hindered by type-Ⅱquantum well structures arising from the mixture of zinc blende(ZB)and wurtzite(WZ)phases and surface defects due to the large surface-to-volume ratio.Achieving GaAs-based NWs with high emission efficiency has become a key research focus.In this study,pre-etched silicon substrates were combined with GaAs/AlGaAs core-shell heterostructure to achieve GaAs-based NWs with good perpendicularity,excellent crystal structures,and high emission efficiency by leveraging the shadowing effect and surface passivation.The primary evidence for this includes the prominent free-exciton emission in the variable-temperature spectra and the low thermal activation energy indicated by the variable-power spectra.The findings of this study suggest that the growth method described herein can be employed to enhance the crystal structure and optical properties of otherⅢ-Ⅴlow-dimensional materials,potentially paving the way for future NW devices.
文摘We design and fabricate a 128 × 128 AlGaAs/GaAs quantum well infrared photodetector focal plane array （FPA）. The device is achieved by metal organic chemical vapor deposition and GaAs integrated circuit processing technology. A test structure of the photodetector with a mesa size of 300μm × 300μm is also made in order to obtain the device parameters. The measured dark current density at 77K is 1.5 × 10^-3A/cm^2 with a bias voltage of 2V. The peak of the responsivity spectrum is at 8.4μm,with a cutoff wavelength of 9μm. The blackbody detectivity is shown to be 3.95 × 10^8 （cm · Hz^1/2）/W. The final FPA is flip-chip bonded on a CMOS read-out integrated circuit. The infrared thermal images of some targets at room temperature background are successfully demonstrated at 80K operating temperature with a ratio of dead pixels of less than 1%.
文摘利用各向异性的湿法刻蚀和侧墙隔离技术实现了发射极金属和基极金属的自对准 ,采用该自对准技术成功地研制出了自对准结构的 Al Ga As/ Ga As异质结双极晶体管 ,器件直流电流增益大于 2 0 ,电流增益截止频率 f T 大于30 GHz,最高振荡频率 fmax大于 5 0 GHz,连续波功率测量表明 :在 1d B增益压缩时 ,单指 HBT可以提供 10 0 m W输出功率 ,对应的功率密度为 6 .6 7W/ m m,功率饱和时最大输出功率 112 m W,对应功率密度为 7.48W/ m m,功率附加效率为 6 7%