SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surfa...SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surface chemistry of these nano particles were characterized by transmission electron microscope,X-ray diffractometer and X-ray photoelectron spectroscope respectively.It was observed that Pd-doping had little effect on the grain sizes of the obtained SnO2 nano particles during the hydrothermal route.During thermal annealing,Pd-doping could restrain the growth of grain sizes below 500℃ while the grain growth was promoted when the temperature increased to above 700℃.XPS results revealed that Pd existed in three chemical states in the as-synthesized sample as Pd^0,Pd^2＋ and Pd^4＋,respectively.Pd^4＋ was the main state which was responsible for improving the gas-sensing property.The optimal Pd-doping concentration for better gas-sensing property and thermal stability was 2.0%-2.5% （mole fraction）.展开更多
Fluorine doped tin oxide SnO2：F thin films were prepared by the spray pyrolysis （SP） technique on glass substrates by using SnC12.2H2O as a precursor and NH4F and HF as doping compounds. A comparison between the pr...Fluorine doped tin oxide SnO2：F thin films were prepared by the spray pyrolysis （SP） technique on glass substrates by using SnC12.2H2O as a precursor and NH4F and HF as doping compounds. A comparison between the properties of the films obtained by using the two doping compounds was performed by using I-V characteristics in the dark at room temperature, AC measurements, and transmittance. It is found that the films prepared by using HF have smaller resistivity, lower impedance and they are less capacitive than films prepared by using NH4F. In addition, these films have higher transmittance, higher optical bandgap energy and narrower Urbach tail width. These results are interesting for the use of SnO2：F as forecontact in CdS/CdTe solar cells.展开更多
A series of three‐dimensionally ordered macroporous(3DOM)SnO2‐based catalysts modified by the cations Ce4+,Mn3+,and Cu2+have been prepared by using a colloidal crystal templating method and tested for soot combustio...A series of three‐dimensionally ordered macroporous(3DOM)SnO2‐based catalysts modified by the cations Ce4+,Mn3+,and Cu2+have been prepared by using a colloidal crystal templating method and tested for soot combustion under loose contact condition.XRD and STEM mapping results confirm that all the secondary metal cations have entered the lattice matrix of tetragonal rutile SnO2 to form non‐continuous solid solutions,thus impeding crystallization and improving the surface areas and pore volumes of the modified catalysts.In comparison with regular SnO2 nanoparticles,the 3DOM SnO2 displays evidently improved activity,testifying that the formation of the 3DOM structure can anchor the soot particulates in the macro‐pores,which ensures that the contact of the soot particles with the active sites on the 3DOM skeleton is more easily formed,thus benefiting the target reaction.With the incorporation of the secondary metal cations,the activity of the catalyst can be further improved due to the formation of more abundant mobile oxygen species.In summary,these effects are believed to be the major factors responsible for the activity of the catalyst.展开更多
Herein, we for the first time doped Nb^5+into the low-temperature(<100°C) SnO2sol-gel route to tailor the electrical property of SnO2 layers and the band alignment between SnO2 and the normally used mixed pero...Herein, we for the first time doped Nb^5+into the low-temperature(<100°C) SnO2sol-gel route to tailor the electrical property of SnO2 layers and the band alignment between SnO2 and the normally used mixed perovskites. The results revealed that proper Nb5+doping increased the conductivity of the SnO2 electron transport layer(ETL), and the conduction band(CB) level of the SnO2 ETL was shifted down to approach the CB level of perovskites, which facilitated the electron injection from perovskite to SnO2, accelerated the charge transport, and reduced the non-radiative recombination, leading to improved power conversion efficiency from18.06% to 19.38%. The Nb^5+doping process provided an efficient route for fabricating high-efficiency perovskite solar cells(PSCs) at a temperature lower than 100°C, and promoted the commercialization progress of PSCs.展开更多
基金Projects(60806032,20975107) supported by the National Natural Science Foundation of ChinaProject(2009R10064) supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars of Education Ministry,China+2 种基金 Project(2009R10064) supported by "Qianjiang Talent Program"Projects(2009A610058,2009A610030) supported by the Ningbo Natural Science Foundation,ChinaProject supported by K.C.WONG Magna Fund in Ningbo University,China
文摘SnO2 nano particles with various Pd-doping concentrations were prepared using a template-free hydrothermal method.The effects of Pd doping on the crystal structure,morphology,microstructure,thermal stability and surface chemistry of these nano particles were characterized by transmission electron microscope,X-ray diffractometer and X-ray photoelectron spectroscope respectively.It was observed that Pd-doping had little effect on the grain sizes of the obtained SnO2 nano particles during the hydrothermal route.During thermal annealing,Pd-doping could restrain the growth of grain sizes below 500℃ while the grain growth was promoted when the temperature increased to above 700℃.XPS results revealed that Pd existed in three chemical states in the as-synthesized sample as Pd^0,Pd^2＋ and Pd^4＋,respectively.Pd^4＋ was the main state which was responsible for improving the gas-sensing property.The optimal Pd-doping concentration for better gas-sensing property and thermal stability was 2.0%-2.5% （mole fraction）.
文摘Fluorine doped tin oxide SnO2：F thin films were prepared by the spray pyrolysis （SP） technique on glass substrates by using SnC12.2H2O as a precursor and NH4F and HF as doping compounds. A comparison between the properties of the films obtained by using the two doping compounds was performed by using I-V characteristics in the dark at room temperature, AC measurements, and transmittance. It is found that the films prepared by using HF have smaller resistivity, lower impedance and they are less capacitive than films prepared by using NH4F. In addition, these films have higher transmittance, higher optical bandgap energy and narrower Urbach tail width. These results are interesting for the use of SnO2：F as forecontact in CdS/CdTe solar cells.
基金the Natural Science Foundation of China(21567016,21503106)the Natural Science Foundation of Jiangxi Province(20171BAB213013)+3 种基金the Education Department Foundation of Jiangxi Province(KJLD14005)National Key Research and Development Program of China(2016YFC0209302)the Innovation Fund Designated for Graduate Students of Jiangxi Province(YC2015-B017)the Innovation Fund Designated for Undergraduate Students of China(201701035)~~
文摘A series of three‐dimensionally ordered macroporous(3DOM)SnO2‐based catalysts modified by the cations Ce4+,Mn3+,and Cu2+have been prepared by using a colloidal crystal templating method and tested for soot combustion under loose contact condition.XRD and STEM mapping results confirm that all the secondary metal cations have entered the lattice matrix of tetragonal rutile SnO2 to form non‐continuous solid solutions,thus impeding crystallization and improving the surface areas and pore volumes of the modified catalysts.In comparison with regular SnO2 nanoparticles,the 3DOM SnO2 displays evidently improved activity,testifying that the formation of the 3DOM structure can anchor the soot particulates in the macro‐pores,which ensures that the contact of the soot particles with the active sites on the 3DOM skeleton is more easily formed,thus benefiting the target reaction.With the incorporation of the secondary metal cations,the activity of the catalyst can be further improved due to the formation of more abundant mobile oxygen species.In summary,these effects are believed to be the major factors responsible for the activity of the catalyst.
基金supported by the National Natural Science Foundation of China (51273104 and 91433205)
文摘Herein, we for the first time doped Nb^5+into the low-temperature(<100°C) SnO2sol-gel route to tailor the electrical property of SnO2 layers and the band alignment between SnO2 and the normally used mixed perovskites. The results revealed that proper Nb5+doping increased the conductivity of the SnO2 electron transport layer(ETL), and the conduction band(CB) level of the SnO2 ETL was shifted down to approach the CB level of perovskites, which facilitated the electron injection from perovskite to SnO2, accelerated the charge transport, and reduced the non-radiative recombination, leading to improved power conversion efficiency from18.06% to 19.38%. The Nb^5+doping process provided an efficient route for fabricating high-efficiency perovskite solar cells(PSCs) at a temperature lower than 100°C, and promoted the commercialization progress of PSCs.