Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) ...Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) (PVA) at 90 degree C and act as plasticizer in the blend films cast from the solution. Only a glass transition temperature is observed for all these blends indicating the formation of compatible blends from these polyesters with PVA. These blends exhibit manifold characteristics such as ionic conductivity, complex formation with metal ions, absorption of moisture and color changes. The electric conductivity of the copolyesters and blends is in the range of 10** minus **6 Scm** minus **1. The blends with PVA forms complexes with Cu**2** plus and Co**2** plus . The coordination structure with two chelate rings is suggested for these polymer blend/metal complexes. (Author abstract) 10 Refs.展开更多
X-ray diffraction line profiles of low density polyethylene(LDPE)/ (ethylene-propylene-octene-1)copolymer(EPO)blends have been analyzed with variance range function method.Theories for determining the microparacrystal...X-ray diffraction line profiles of low density polyethylene(LDPE)/ (ethylene-propylene-octene-1)copolymer(EPO)blends have been analyzed with variance range function method.Theories for determining the microparacrystallite size and the distortion parameter from single reflection have been described,and the value of these two parameters at (110)and(200)directions have been determined.展开更多
The physical and mechanical properties of blends composed of two kinds of epoxy resins of different numbers of functional groups and chemical structure were studied. One of the resins was a bifunctional epoxy resin ba...The physical and mechanical properties of blends composed of two kinds of epoxy resins of different numbers of functional groups and chemical structure were studied. One of the resins was a bifunctional epoxy resin based on diglycidyl ether of bisphenol A and the other resin was a multifunctional epoxy novolac resin. Attempt was made to establish a correlation between the structure and the final properties of cured epoxy samples. The blend samples containing high fraction of multifunctional epoxy resin showed higher solvent resistance and lower flexural modulus compared with the blends containing high fraction of bifunctional epoxy resin. The epoxy blends showed significantly higher ductility under bending test than the neat epoxy samples. The compressive modulus and strength increased with increasing of multifunctional epoxy in the samples, probably due to enhanced cross-link density and molecular weight. Morphological analysis revealed the presence of inhomogeneous sub-micrometer structures in all samples. The epoxy blends exhibited significantly higher fracture toughness（by 23% at most） compared with the neat samples. The improvement of the fracture toughness was attributed to the stick-slip mechanism for crack growth and activation of shear yielding and plastic deformation around the crack growth trajectories for samples with higher content of bifunctional epoxy resin as evidenced by fractography study.展开更多
The thermal decomposition analysis of coal-pharmaceutical waste sludge,coal-sewage waste sludge blends and coal-sunflower seed husk blends are studied by TG dynamic runs at the heating rate of 20 ℃/min within the tem...The thermal decomposition analysis of coal-pharmaceutical waste sludge,coal-sewage waste sludge blends and coal-sunflower seed husk blends are studied by TG dynamic runs at the heating rate of 20 ℃/min within the temperature range of 25 ℃-900 ℃.The effect of different kinetic models on the determination of kinetic parameters of thermal decomposition has been investigated.Results show that for coal-pharmaceutical sludge blend,coal-sewage sludge blend and coal-sunflower seed husk blend the optimal model functions are the three-dimensional diffusion reaction,2-dimensional and 3-diemensional nucleation and growth reactions,respectively.The Arrhenius kinetic parameters of the pre-exponential factor and activation energy of blends,as well waste sludge and sunflower seed husk only are proposed.展开更多
文摘Copolyesters having secondary and tertiary amine salt groups in the main and side chains are prepared by chemoselective polymerization. These copolyesters are soluble in a 10% aqueous solution of poly(vinyl alcohol) (PVA) at 90 degree C and act as plasticizer in the blend films cast from the solution. Only a glass transition temperature is observed for all these blends indicating the formation of compatible blends from these polyesters with PVA. These blends exhibit manifold characteristics such as ionic conductivity, complex formation with metal ions, absorption of moisture and color changes. The electric conductivity of the copolyesters and blends is in the range of 10** minus **6 Scm** minus **1. The blends with PVA forms complexes with Cu**2** plus and Co**2** plus . The coordination structure with two chelate rings is suggested for these polymer blend/metal complexes. (Author abstract) 10 Refs.
文摘X-ray diffraction line profiles of low density polyethylene(LDPE)/ (ethylene-propylene-octene-1)copolymer(EPO)blends have been analyzed with variance range function method.Theories for determining the microparacrystallite size and the distortion parameter from single reflection have been described,and the value of these two parameters at (110)and(200)directions have been determined.
文摘The physical and mechanical properties of blends composed of two kinds of epoxy resins of different numbers of functional groups and chemical structure were studied. One of the resins was a bifunctional epoxy resin based on diglycidyl ether of bisphenol A and the other resin was a multifunctional epoxy novolac resin. Attempt was made to establish a correlation between the structure and the final properties of cured epoxy samples. The blend samples containing high fraction of multifunctional epoxy resin showed higher solvent resistance and lower flexural modulus compared with the blends containing high fraction of bifunctional epoxy resin. The epoxy blends showed significantly higher ductility under bending test than the neat epoxy samples. The compressive modulus and strength increased with increasing of multifunctional epoxy in the samples, probably due to enhanced cross-link density and molecular weight. Morphological analysis revealed the presence of inhomogeneous sub-micrometer structures in all samples. The epoxy blends exhibited significantly higher fracture toughness（by 23% at most） compared with the neat samples. The improvement of the fracture toughness was attributed to the stick-slip mechanism for crack growth and activation of shear yielding and plastic deformation around the crack growth trajectories for samples with higher content of bifunctional epoxy resin as evidenced by fractography study.
基金Sponsored by the National Natural Science Foundation of China(Grant No.21076043)China Postdoctoral Science Foundation(Grant No.20090460070)+1 种基金Heilongjiang Province Postdoctoral Science Foundation(Grant No.LBH-Z09292)Educational Committee of Heilongjiang Privince Science Foundation(Grant No.11551006)
文摘The thermal decomposition analysis of coal-pharmaceutical waste sludge,coal-sewage waste sludge blends and coal-sunflower seed husk blends are studied by TG dynamic runs at the heating rate of 20 ℃/min within the temperature range of 25 ℃-900 ℃.The effect of different kinetic models on the determination of kinetic parameters of thermal decomposition has been investigated.Results show that for coal-pharmaceutical sludge blend,coal-sewage sludge blend and coal-sunflower seed husk blend the optimal model functions are the three-dimensional diffusion reaction,2-dimensional and 3-diemensional nucleation and growth reactions,respectively.The Arrhenius kinetic parameters of the pre-exponential factor and activation energy of blends,as well waste sludge and sunflower seed husk only are proposed.