A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic re...A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic reduction（SCR） performance and SO2-resistant ability of TiO2-SiO2-WO3 were greatly enhanced by the introduction of cerium. The catalyst containing 10% CeO2 showed the highest NO conversion in a wide temperature range and good N2 selectivity with broad operation temperature window at the gas hourly space velocity（GHSV） of 30000 h–1, which was a very promising catalyst for NOx abatement from diesel engine exhaust. The catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy with energy dispersive X-ray spectroscopy（SEM-EDS）, N2 adsorption-desorption（BET） and X-ray photoelectron spectroscopy（XPS）. The characterization results showed that the bigger pore radius, higher surface atomic concentration and dispersion of Ce and the abundant adsorbed oxygen on the surface of catalyst contributed to the best NH3-SCR performance of CeO2/TiO2-SiO2-WO3 catalyst containing 10% CeO2.展开更多
The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel...The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.展开更多
8wt%WO3/SiO2 metathesis （disproportionation） catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-deso...8wt%WO3/SiO2 metathesis （disproportionation） catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, UV-visible diffuse reflectance spectroscopy （DRS） and scanning transmission electron microscopy-high-angle annular dark field （STEM HAADF）. The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure： The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.展开更多
基金supported by the National Natural Science Foundation of China(21173153)the National High Technology Research and Development Program of China(863 project)(2013AA065304)
文摘A series of catalysts were prepared by doping different loadings of CeO2 over TiO2-SiO2-WO3 and used for the selective catalytic reduction of NOx by NH3. The experimental results showed that the selective catalytic reduction（SCR） performance and SO2-resistant ability of TiO2-SiO2-WO3 were greatly enhanced by the introduction of cerium. The catalyst containing 10% CeO2 showed the highest NO conversion in a wide temperature range and good N2 selectivity with broad operation temperature window at the gas hourly space velocity（GHSV） of 30000 h–1, which was a very promising catalyst for NOx abatement from diesel engine exhaust. The catalysts were characterized by X-ray diffraction（XRD）, scanning electron microscopy with energy dispersive X-ray spectroscopy（SEM-EDS）, N2 adsorption-desorption（BET） and X-ray photoelectron spectroscopy（XPS）. The characterization results showed that the bigger pore radius, higher surface atomic concentration and dispersion of Ce and the abundant adsorbed oxygen on the surface of catalyst contributed to the best NH3-SCR performance of CeO2/TiO2-SiO2-WO3 catalyst containing 10% CeO2.
基金financially supported by the National Key Research and Development Program of China (No. 2016YFC0204300)the National High Technology Research and Development Program of China (No. 2015AA034603)+2 种基金the National Natural Science Foundation of China (Nos. 21333003 and 21571061)the "Shu Guang" Project of the Shanghai Municipal Education Commission (No. 12SG29)the Commission of Science and Technology of Shanghai Municipality (No. 15DZ1205305)
文摘The selective catalytic reduction of NOV with NH3 (NH3-SCR) is a very effective technology to control the emission of NOA, and the thermal stability of NH3-SCR catalyst is very important for removal of NOV from diesel engines. In this work, V2O5/WO3-TiO2 (VWT) and SiO2- doped V2O5/WO3-TiO2 (VWTSi10)) catalysts were prepared by impregnation method and characterized by Brunauer- Emmett-Teller (BET), X-ray diffraction (XRD), Raman, temperature programmed reduction by hydrogen (H2-TPR), X-ray photoelectron spectroscopy (XPS) and temperature programmed desorption by ammonia (NH3- TPD). The doping of SiO2 promotes the thermal stability of V2O5/WO3-TiO? for NH3-SCR significantly. After calcination at 650 °C for 50 h, the operation window of 10% SiO2-doped V2O5/WO3-TiO2 is 220-480 °C, while the maximum NOV conversion on V2O5/WO3-TiO2 is about 77%. The presenee of SiO2 obviously blocks the transformation of TiO2 from anatase to rutile and stabilizes the dispersion of VOv and WO3 on the surface. It is available for the existence of V44 and the amount of surface acid sites increases, which inhabits the NH3 oxidation at the high temperature range and promotes NH3-SCR activity.
文摘8wt%WO3/SiO2 metathesis （disproportionation） catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, UV-visible diffuse reflectance spectroscopy （DRS） and scanning transmission electron microscopy-high-angle annular dark field （STEM HAADF）. The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure： The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.