The influence of the baked temperature for TiO 2 ultrafine particles on the photocatalytic oxidation reaction of SO 2 was investigated. The photocatalytic activity of TiO 2 baked at 320 ℃ is higher than that at other...The influence of the baked temperature for TiO 2 ultrafine particles on the photocatalytic oxidation reaction of SO 2 was investigated. The photocatalytic activity of TiO 2 baked at 320 ℃ is higher than that at other temperatures(480 ℃, 550 ℃). It may be explained by the surface state of TiO 2, increasing the content of surface hydroxyl is helpful to enhance the photocatalytic activity. According to the experimental results, the first order kinetic reaction and the mechanism of the reaction were suggested, also the rate constants and half life time were reported.展开更多
A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
文摘The influence of the baked temperature for TiO 2 ultrafine particles on the photocatalytic oxidation reaction of SO 2 was investigated. The photocatalytic activity of TiO 2 baked at 320 ℃ is higher than that at other temperatures(480 ℃, 550 ℃). It may be explained by the surface state of TiO 2, increasing the content of surface hydroxyl is helpful to enhance the photocatalytic activity. According to the experimental results, the first order kinetic reaction and the mechanism of the reaction were suggested, also the rate constants and half life time were reported.
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.