摘要
用水蒸气沉淀法制备了SiO2 偏氟乙烯 六氟丙烯共聚物 [P(VDF HFP) ]复合微孔型聚合物电解质 ,并研究了纳米SiO2 的加入对微孔结构及复合微孔型聚合物电解质性能的影响 .SEM观察发现当纳米SiO2 的添加量大于 0 1倍聚合物质量时 ,可以在微孔中观察到纳米粒子的严重团聚现象 .电导率的测量表明添加 0 0 5倍聚合物质量的纳米SiO2 后 ,微孔型聚合物电解质的电导率有明显提高 ,但进一步增大添加量后 ,电导率有所下降 .另外 ,实验发现添加纳米SiO2 可以明显提高微孔型聚合物电解质与锂金属电极之间的界面稳定性 ,特别是添加量为 0 0 5倍聚合物质量时的效果良好 .
SiO2/vinylidine fluoride-hexafluropropene copolymer [ P ( VDF-HFP) composite porous polymer electrolytes were prepared by phase inversion induced by water vapor. The influence of nano-SiO2 on the porous structure and performance of the porous polymer electrolytes was studied. The results show that when the weight ratio of SiO2 to polymer is about 0.05, the porous polymer electrolytes have improved conductivity and interfacial stability against lithium metal electrodes; but when the amount of SiO2 is further increased, serious aggregation of nano-SiO2 can be found in the pores, and the performance of the porous polymer electrolytes is reduced.
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2004年第3期350-354,共5页
Acta Polymerica Sinica
基金
清华大学 985材料科学与工程研究院重点项目"燃料电池与新型二次电池材料及应用"资助项目 (项目号ZA2 1)