摘要
对Al-Zn-Mg-Cu系超高强铝合金采用Zr细化组织处理后,研究了管材的组织和性能之间的关系,通过金相组织观察和断口扫描,分析了影响管材断裂韧性Kc值的主要因素。
After Zr refining structure treatment of Al-Zn-Mg-Cu super-high strength aluminium alloy was done,relation betwee n structure and property was studied.The main factors of affecting fracture tou ghness K c were analysed through metallographical structure and fracture scanning.
出处
《轻合金加工技术》
CAS
2003年第12期23-25,共3页
Light Alloy Fabrication Technology
关键词
超高强铝合金
管材
组织
性能
断裂韧性
Zr细化组织处理
Al-Zn-Mg-Cu super high strength aluminium alloy pipe
Zr refining str ucture treatment
fracture toughness