摘要
采用化学分析、金相检验和断口扫描等方法对不锈钢开裂的原因进行分析。结果表明,钢管表面氯离子的富集,引起了钢管承受张应力部位应力腐蚀开裂。
Chemical composition analysis,microstructure examination and fracture analysis were conducted to clarify reasons for crack of stainless steel.The results show that： the crack of stainless tube is caused by the stress corrosion at the tension stress side of the tube,which resulted from accumulation of Cl on surface of the tube.
出处
《物理测试》
CAS
2010年第1期53-55,62,共4页
Physics Examination and Testing
关键词
钢管
应力腐蚀
裂纹
失效分析
stainless tube
stress corrosion
crack
failure analysis