摘要
以多官能团有机锂为引发体系 ,一步聚合制备了偶联度为 10 0 %的锡偶联型溶聚丁苯橡胶(S10 0 )。将其与NR共混 ,研究了共混物混炼胶的加工性能和硫化胶的物理机械性能。结果表明 ,NR的加入有利于S10 0 加工性能的改善和混炼效果的提高 ,并且在NR用量不少于 6 0份 (质量 ,下同 )时 ,可以提高制品的尺寸稳定性 ;S10 0 并用NR后 ,硫化胶的 30 0 %定伸应力、拉伸强度、撕裂强度、扯断伸长率和永久变形有所提高 ,但试样动态生热增加 ,内耗增大 ,耐磨性降低。兼顾试样的加工性能 ,NR用量以2 0～ 5
The processability, mechanical properties and dynamical properties of tin coupled SSBR with 100% of coupling degree (S100)/NR blend were studied. The results showed that NR could improve the processability of S100, tensile strength, modulus at 300%, tear strength, elongation at break and permanent set, but damage abrasion resistance and dynamical properties. The optimum amount of NR was 20-50 phr.