A simple method to prepare the non-spherical gold particles was developed. The result solution included trigonal, truncated trigonal, hexagonal layers, and a pseudo-pentagonal shaped gold nanocrystals. The key factor is to control the relative rates of nucleation and cluster growth in this method. These attributes make seeding growth method as a useful tool in the fabrication of colloidal metal materials. A longitudinal plasmon resonance of 866 nm was observed, which is in the near-IR spectral regions (600-1000 nm). The excellent optical properties as near-IR labels are used to develop highly sensitive analysis method.
A simple method to prepare the non-spherical gold particles was developed. The result solution included trigonal, truncated trigonal, hexagonal layers, and a pseudo-pentagonal shaped gold nanocrystals. The key factor is to control the relative rates of nucleation and cluster growth in this method. These attributes make seeding growth method as a useful tool in the fabrication of colloidal metal materials. A longitudinal plasmon resonance of 866 nm was observed, which is in the near-IR spectral regions (600-1000 nm). The excellent optical properties as near-IR labels are used to develop highly sensitive analysis method.