摘要
采用基于密度泛函理论的相对论性离散变分和嵌入团簇方法 ,计算了掺钇PbWO4 晶体中多种相关缺陷的电荷分布和不同团簇缺陷结合能 ,由能量最低原理发现 [2 (Y3+Pb) V″Pb]缺陷在各相关缺陷形式中最为稳定 .并运用过渡态方法计算了轨道跃迁的激发能 ,算出掺Y后晶体中O2p→Y4d的跃迁能量为 3 9eV ,表明掺Y不会引起晶体中35 0nm和 4 2 0nm吸收 .从掺Y对PbWO4 晶体电子结构的影响来看 。
The electronic structures and binding energy of the defects related to gamma(3+) dopants in PbWO4 crystals have been investigated by the relativistic self-consistent discrete variational embedded cluster method. The results show that [2(Y-Pb(3+)) - V-Pb'] is more stable than the other Y3+ related defects. Using the transition state method, we find that the transition energy of O2p-->Y5d is about 3.9eV. This signifies that Y3+ ions will not result in the absorptions at 350nm and 420nm in the PbWO4 crystal. Moreover, the effect on electronic structure in PbWO4 caused by Y dopants is different from that caused by La dopants.
出处
《物理学报》
SCIE
EI
CAS
CSCD
北大核心
2003年第9期2274-2279,共6页
Acta Physica Sinica
基金
国家自然科学基金 (批准号 :197740 43 )
教育部高等学校优秀青年教师教学科研奖励计划(教人司 (2 0 0 2 )123 )
上海市教育委员会重点学科研究项目
曙光计划(批准号:0 2SG19)
青年教师项目(批准号:0 1QN18)资助的课题~~