用电沉积法制备Ni-La-P合金。XRD衍射证明此合金为非晶态结构。以此为阴极电解还原葡萄糖,结果表明Ni-La-P非晶态合金具有高的电催化活性。当温度为30℃,电流为0.4A,电解90min,葡萄糖转化率达82.41%,电流效率达91.3%。
The NiLaP alloys were prepared by means of electrodisposition They were proved to be amorphous alloys by XRD Using these alloys as cathode, glucose was reduced to sorbtial and current efficient were measured It is found that its catalytic achievement was outclass than that of Raney-Ni catalyst The results showed that the best techniques of electrocatalytic reduction of glucose are: T=30℃,I=04A,t=90min