The self-assembly between poly(4-diazonium styrene) (PDS) and poly(sodiumsulfonate styrene)(PSS) was investigated.The mutilayer ult ra thin films were fabricated layer-by-layer successfully from PDS and PSS.Af ter heating for 10 min at 70℃ the multilayer film became very stable towards po lar solvents.No considerable changes were observed for the heated film soaked i n DMF (20℃) for 48 h,while the unheated film almost destroyed at same conditio n.The dramatic improvement in stability of the film towards polar solvents shou ld be attributed to the conversion of bonds between the layers of the film from ionic bond to covalent bond under heating.Y(4 DIAZONIUMSTYRENE)ANDPOLY(SODIUMSULFONATESTYRENE)YANGZhaohui,JIANGWei,CAOWeixiao(CollegeofChemistryandMolecularEngineering ,PekingUniversity ,Beijing 10 0 871)Abstract Theself assemblybetweenpoly( 4 diazoniumstyrene) (PDS)andpoly(sodiumsulfonatestyrene) (PSS)wasinvestigated .Themutilayerultrathinfilmswerefabricatedlayer by layersuccessfullyfromPDSandPSS .Afterheatingfor 1 0minat 70℃themultilayerfilmbecameverystabletowardspolarsolvents.NoconsiderablechangeswereobservedfortheheatedfilmsoakedinDMF ( 2 0℃ )for48h ,whiletheunheatedfilmalmostdestroyedatsamecondition.Thedramaticimprovementinstabilityofthefilmtowardspolarsolventsshouldbeattributedtotheconversionofbondsbetweenthelayersofthefilmfromionicbondtocovalentbondunderheating .Keywords Poly( 4 diazoniumstyrene) 。
The self-assembly between poly(4-diazonium styrene) (PDS) and poly(sodiumsulfonate styrene)(PSS) was investigated.The mutilayer ult ra thin films were fabricated layer-by-layer successfully from PDS and PSS.Af ter heating for 10 min at 70℃ the multilayer film became very stable towards po lar solvents.No considerable changes were observed for the heated film soaked i n DMF (20℃) for 48 h,while the unheated film almost destroyed at same conditio n.The dramatic improvement in stability of the film towards polar solvents shou ld be attributed to the conversion of bonds between the layers of the film from ionic bond to covalent bond under heating.Y(4 DIAZONIUMSTYRENE)ANDPOLY(SODIUMSULFONATESTYRENE)YANGZhaohui,JIANGWei,CAOWeixiao(CollegeofChemistryandMolecularEngineering ,PekingUniversity ,Beijing 10 0 871)Abstract Theself assemblybetweenpoly( 4 diazoniumstyrene) (PDS)andpoly(sodiumsulfonatestyrene) (PSS)wasinvestigated .Themutilayerultrathinfilmswerefabricatedlayer by layersuccessfullyfromPDSandPSS .Afterheatingfor 1 0minat 70℃themultilayerfilmbecameverystabletowardspolarsolvents.NoconsiderablechangeswereobservedfortheheatedfilmsoakedinDMF ( 2 0℃ )for48h ,whiletheunheatedfilmalmostdestroyedatsamecondition.Thedramaticimprovementinstabilityofthefilmtowardspolarsolventsshouldbeattributedtotheconversionofbondsbetweenthelayersofthefilmfromionicbondtocovalentbondunderheating .Keywords Poly( 4 diazoniumstyrene) ,Poly(sod
出处
《高分子学报》
SCIE
CAS
CSCD
北大核心
2003年第3期442-444,共3页
Acta Polymerica Sinica
基金
国家自然科学基金 (基金号 2 0 2 740 0 2和 5 0 1730 0 2 )资助项目
关键词
聚4-重氮基苯乙烯
聚苯乙烯磺酸钠
自组装
超薄膜
LB膜
交联结构
Poly(4-diazonium styrene), Poly(sodiumsulfonate st yrene), Self assembly films PPAGESS STUDY ON SYNTHESIS AND PROPERTIES OF SELF-YELLOWISHED LATEXES WITH PENDANT AZO GROUPS$$$$ WANG Jingxia, KAN Chengyou, LIU Deshan （Department of C