羧基纤维素(钠盐,以下简称CMC)是一种重要的水溶性聚电解质。本文在传统溶媒法的基础上,采用乙醇作溶剂的两段加碱法新工艺制备CMC。研究表明,在低浴比(乙醇与纤维素质量比为2.04～2.45)条件下,采用新工艺制得的CMC具有较好的取代均一性和良好的性能:并用酶降解的方法,通过还原值测定,对CMC的取代基沿分子链的分布进行了表征;此外,对CMC的一些性能进行了测定,同时对其热稳定性进行了研究。
Carboxymethylcellulose(CMC) is one of the improtant water soluble polyelectrolyte. In this paper, CMC were prepared by the two-stage NaOH addition process. It was found that the CMC having a uniform substituent distribution with DS of about 0.9 and viscosity aqueous solution of 0.02 mass fraction in the range of 900-1000MPa·s had be obtained by the two-stage NaOH addition process at low ratio of ethyl alcholl: cellulose being 2.04 to 2.45 mass ratio. The distribution of substituents along the cellulose chains were characterized through the analyses of enzymic hydrolysis. The results showed that the average number of structural unit in a substituted block (L_(Sn)) for the two-stage NaOH addition process was longer than that for the conventional addition manner and the substitutio index(SI) was higher than that for the onventional addition manner. The DS, viscosity, sodium chloride and moisture content were measured by standard method. And the heat-stability of CMC had also be studied.
出处
《广州化学》
CAS
1992年第2期38-46,共9页
Guangzhou Chemistry