摘要
聚醚醚酮是一种高性能聚合物,其优异的性能使其在工程塑料中处于领先地位。近年来,3D打印技术渐渐成熟,因为其节省材料、快速制造的特点被应用于许多领域。采用熔融沉积成型计算打印聚醚醚酮(PEEK),讨论了在打印温度为400℃、打印速度为50 mm/s、打印层高为0.2 mm参数下,打印密度为40%、50%、60%、70%时PEEK的拉伸和冲击性能,研究结果表明,50%打印密度下PEEK的力学性能最优。
Polyether ether ketone is a high performance polymer because its excellent properties place it at the top of engineering plastics.In recent years,3D printing technology has gradually matured,because of its material saving,rapid manufacturing characteristics are applied to many fields.The tensile properties and impact properties of PEEK at printing temperature of 400℃,printing speed of 50 mm/s,printing layer of 0.2 mm and printing density of 40%,50%,60%and 70%were discussed.The research results show that PEEK has the best mechanical properties at printing density of 50%.
作者
孙野
郭纯
黄光灿
SUN Ye;GUO Chun;HUANG Guang-can(College of Mechanical Engineering,Anhui Science and Technology University,Fengyang 233100,Anhui,China)
出处
《合成纤维》
2025年第2期72-76,共5页
Synthetic Fiber in China
基金
大学生创新创业训练计划项目(S202310879131)
安徽省高校自然科学研究项目重大项目(2023AH040273)
安徽省高校优秀拔尖人才项目(gxbjZD2022046)
安徽省高校科学研究项目(YJS20210558)
安徽省高校协同创新项目(GXXT-2023-025、GXXT-2023-026)
蚌埠市科技计划项目(2023gx09)
安徽科技学院学术和技术带头人后备人选项目(202101)
安徽省自然科学基金项目(1908085QE174)
安徽科技学院人才项目(RCYJ201905)。
关键词
聚醚醚酮
熔融沉积
3D打印
力学性能
polyether ether ketone
melt deposition
3D printing
mechanical property