摘要
The mechanical and fatigue properties of SA508-Ⅳ steel with martensite and granular bainite, respectively, were studied. The mechanical tests results showed that the ultimate tensile strength and impact toughness of the specimen with martensite were 830 MPa and 158 J, respectively, and those of the specimen with granular bainite were 811 MPa and 115 J, respectively. The former had higher tensile strength and impact toughness than the latter. The impact tests results showed that the former belonged to typical dimple fracture, while the latter belonged to brittle fracture. The fatigue tests results showed that the fatigue life of the specimen with martensite was 2717 cycles, and that of the specimen with granular bainite was 1545 cycles under the strain amplitude of ± 0.45%. The specimen with martensite had fewer crack initiation points, narrower fatigue striations separation, and larger volume fraction of high-angle grain boundaries than the latter. The fewer crack initiation points meant fewer fatigue cracks, the narrower fatigue striations separation meant slower crack propagation rate, and the larger volume fraction of high-angle grain boundaries could more effectively hinder fatigue crack propagation. Based on these facts, the fatigue life of the specimen with martensite was higher than that of the specimen with granular bainite.
基金
the Beijing Municipal Natural Science Foundation under No.2162026 and the 863 Program of China under Nos.2008AA031702 and 2012AA03A507 for financial support.