This study focused on the manufacture of microcrystalline cellulose(MCC)from wheat straw using environmentally-friendly solvents.Raw cellulose was separated from wheat straw after thermal decomposition of lignin followed by dissolution of lignin using a recyclable ethanol/acetic acid/water solvent system.Then,pure cellulose was produced using a four-step refining process,including chelating,O_(3),H_(2)O_(2),and xylanase treatments.Finally,MCC was obtained through hydrolysis,drying,and mechanical treatments.The effects of acetic acid,O_(3),H_(2)O_(2),NaOH,pretreatment time,and temperature on the properties of wheat straw cellulose(including Kappa number,yield,α-cellulose content,crystallinity,KMnO4 value,degree of polymerization(DP),and brightness)were investigated.The results showed that the addition of acetic acid enhanced lignin removal and hemicellulose degradation,improving the purity of the raw cellulose.The optimized acetic acid dosage in the wheat straw thermal decomposition step was 2%(w/w).The optimized O_(3)dosage was 1.2%(w/w).The optimized conditions for H_(2)O_(2)treatment were found to be 3%(w/w)H_(2)O_(2)and 1.8%(w/w)NaOH at 70°C for 120 min.The KMnO4 value was 2.0,brightness was 84.1%ISO,the viscosity was 934 mL/g,and the DP was 626 for refined cellulose.Xylanase effectively improved theα-cellulose content of wheat straw cellulose.With an optimized xylanase dosage of 1.5 IU/g,theα-cellulose content was 94.7%,the brightness was 85.6%ISO,and the DP was 615 for wheat straw cellulose.
基金
the Doctoral Program of Higher Education Projects(for the priority development areas)by Ministry of Education of China(Grant No.20126125130001)
State Key Laboratory of Pulp and Paper Engineering open foundation(Grant No.201505)
the Doctoral Scientific Research Foundation(Grant No.BJ13-02)by Shaanxi University of Science and Technology.