为了获得最佳的供氧和粉剂消耗与温度的关系。国内某钢厂采用专用炉顶吹氧+喷粉搅拌脱磷工艺为AOD炉提供优质的低磷铁水冶炼不锈钢,实现了新型一步法冶炼不锈钢工艺。生产实践表明,随着喷吹钝化石灰粉和铁皮球用量的增加,脱磷率逐渐升高,当石灰喷吹量为10~12kg/t、铁皮球消耗量为25.0~37.5kg/t、供氧量为300~400m3时,脱磷率在85%以上;脱磷率随着钙氧比的增大而减小,当w(CaO)/w(Fe2O3)为0.8时达到最大值,钙氧比为0.8~1.4时脱磷率大部分在85%以上,钙氧比超过1.4时效果降低。
In order to obtain the best oxygen supply and the relationship between powder consumption and temperature.A new one-step process of the stainless steel smelting with low phosphorus hot metal was realized in a domestic steel plant using a special top blowing oxygen + powder injection agitation dephosphorization process to provide AOD furnace with the high-quality stainless steel smelting with low phosphorus hot metal.The production practice showed that the dephosphorization rate increased with the increasing of the dosage of passivated lime powder and iron balls.When the dosage of lime injection was 10-12 kg/t,the consumption of iron balls was 25.0-37.5 kg/t and the oxygen supply was 300-400 m3,the dephosphorization rate was above 85%,and the dephosphorization rate decreased with the increasing of w(CaO)/w(Fe2 O3).The dephosphorization rate was the largest when w(CaO)/w(Fe2 O3)=0.8,most of the dephosphorization rate was over 85% when the w(CaO)/w(Fe2 O3)between 0.8 and1.4,and when the w(CaO)/w(Fe2 O3)more than 1.4,the effect was reduced.
作者
赵斌
吴巍
吴伟
汪成义
崔怀周
ZHAO Bin;WU Wei;WU Wei;WANG Cheng-yi;CUI Huai-zhou(Institute of Metallurgical Technology,Central Iron and Steel Research Institute,Beijing 100081,China)
出处
《钢铁》
CAS
CSCD
北大核心
2019年第11期33-39,共7页
Iron and Steel
基金
北京市自然科学基金面上项目资助项目（2172057）
关键词
炉顶吹氧+喷粉搅拌
铁水脱磷
钙氧比
脱磷率
top blowing oxygen+powder injection mixing
hot metal dephosphorization
w(CaO)/w(Fe2O3)
dephosphorization rate