摘要
The wear and friction properties of Ti3SiC2-based materials were studied using the pin-on-disc method. The friction coefficient of Ti3SiC2-based material was not very sensitive to normal load, the steady state value, μ, increased from 0.4 to 0.5 when the normal load increased from 7.7 N to 14.7 N. The wear volume for Ti3SiC2 disc increased with increasing normal load or sliding distance in the tests. The average wear rate of Ti3SiC2-based material was 9.9×10-5 mm3/Nm. The debris on the Ti3SiC2 disc was essentially made up of Ti3SiC2 and steel pin materials, while the debris on the steel sliders was generally pin material. The wear mechanism was concluded as the fracture and delamination of Ti3SiC2-based materials followed by adhesive wear of steel sliders.