摘要
采用标准陶瓷工艺 ,并进行湿压磁场成型和氧气氛烧结 ,制备了目前尚未见报道的高取向度 ,低介电损耗的各向异性Sr0 .95Ca0 .0 5Fe1 2 O1 9多晶六角铁氧体。研究了它们的比饱和磁化强度 (δs)、磁晶各向异性场 (HA)同温度 (T)的变化关系 。
Magnetic anisotropic polycrystalline Sr 0.95 Ca 0.05 Fe 12 O 19 hexaferrite have been prepared with high orientation degrees f and low dielectric loss tg δ ε by standard ceramic techniques with magnetic alignment of the grains c axes during wet pressing and in flowing oxygen sintering. We have studied change of its saturation magnetization M s and anisotropy field with temperature, and deeply discussed its orientation degree.