Main attention of this paper was devoted to studying the effect of solidification texture on microstructure（phase constituents,grain morphology,and magnetic domain structure） of polycrystalline Fe_（82）Ga_（18） sample.The alloy was melted using button arc melting and solidified in water-cooled copper mold.Optical microscope（OM） results confirm the development of large columnar grains in the solidification microstructure.Phase constitution and magnetic domain structures of the sample were studied by X-ray diffraction（XRD） and magnetic force microscopy（MFM）.Results show a single-phase solid solution with an A2 structure for the sample which consists of regularly aligned magnetic domains.Although some maze-like subdomains are found in few regions,well-aligned stripe-like domains are predominant patterns in the sample.It demonstrates the high dependence of grain morphology and magnetic domain structure upon a preferred crystallographic direction during solidification.
Main attention of this paper was devoted to studying the effect of solidification texture on microstructure（phase constituents,grain morphology,and magnetic domain structure） of polycrystalline Fe_（82）Ga_（18） sample.The alloy was melted using button arc melting and solidified in water-cooled copper mold.Optical microscope（OM） results confirm the development of large columnar grains in the solidification microstructure.Phase constitution and magnetic domain structures of the sample were studied by X-ray diffraction（XRD） and magnetic force microscopy（MFM）.Results show a single-phase solid solution with an A2 structure for the sample which consists of regularly aligned magnetic domains.Although some maze-like subdomains are found in few regions,well-aligned stripe-like domains are predominant patterns in the sample.It demonstrates the high dependence of grain morphology and magnetic domain structure upon a preferred crystallographic direction during solidification.
基金
support of Center of Excellence for High Performance Materials (CEPMAT) at University of Tehran, Sahand University of Technology