摘要
High-temperature performance tests of chromium-containing stuffing sand for a steel ladle w ith different ratios w ere performed. A high-temperature simulation test furnace w as used to analyze the influence of the composition ratio of ladle filler sand and sintering time on the high-temperature compression resistance of chromium-containing stuffing sand in the temperature range of 1 500- 1 600 ℃. The results show that the refractoriness of ladle filler sand w as the low est（ only 1 610 ℃） w hen the composition ratio of chromite sand and silica sand w as 6∶ 4. M oreover,the high-temperature compression resistance w as high w hen the content of chromite sand w as at 70%; the resistance increased w ith increasing sintering time. When the sintering time w as extended at a temperature of 1 600 ℃,the high-temperature compression resistance of ladle filler sand first increased and then decreased after being overburnt.
High-temperature performance tests of chromium-containing stuffing sand for a steel ladle w ith different ratios w ere performed. A high-temperature simulation test furnace w as used to analyze the influence of the composition ratio of ladle filler sand and sintering time on the high-temperature compression resistance of chromium-containing stuffing sand in the temperature range of 1 500- 1 600 ℃. The results show that the refractoriness of ladle filler sand w as the low est（ only 1 610 ℃） w hen the composition ratio of chromite sand and silica sand w as 6∶ 4. M oreover,the high-temperature compression resistance w as high w hen the content of chromite sand w as at 70%; the resistance increased w ith increasing sintering time. When the sintering time w as extended at a temperature of 1 600 ℃,the high-temperature compression resistance of ladle filler sand first increased and then decreased after being overburnt.