针对水泥路面修补后开放交通时间偏长、耐久性较差和施工工艺复杂的问题,采用固体复合激发剂、粉煤灰和偏高岭土及其他外加剂制备一种地聚合物水泥快速修补材料,并对其混凝土力学性能、界面粘结性能、收缩率、抗冻性能进行测试。结果表明,当掺入10%的复合激发剂和10%的普通硅酸盐水泥时,地聚合物水泥的早期力学性能达到最优,所制备的地聚合物水泥混凝土修补材料具有快凝早强和优良的耐久性等特点,扫描电子显微镜(SEM)微观分析表明,由于碱激发反应和未激发粉煤灰的填充效应,地聚合物水泥混凝土具有致密的微观结构。
In order to solve long opening-to-traffic time,poor durability and complex process of concrete pavement repaired problem,a kind of rapid repair geopolymer material was prepared using the solid composite activator,fly ash,metakaolin and other admixtures.The properties of the working performance,mechanical properties,bonding performance between New and old Concrete,shrinkage,frost resistance of geopolymer-cement-concrete were tested.The experimental results show that with 10% compound activators and 10% ordinary Portland cement,the early mechanical properties of the geopolymer cement can achieve the optimal;the rapid repair geopolymer-cement-concrete has the advantages of quick setting early strength and excellent durability.The scanning electron microscopy（SEM）results indicate that the geopolymer-cement-concrete has micro compact structure as the result of the filling effect of inactivated fly ash and alkali activated reaction.
出处
《武汉理工大学学报》
CAS
CSCD
北大核心
2014年第5期49-54,共6页
Journal of Wuhan University of Technology
基金
交通运输部西部交通建设科技项目(20113188121720)
中央高校基本科研业务费专项资金(CHD2012JC071)