分析了原位生成含钛复相陶瓷TiB2 -TiC(TT) ,TiB2 -TiCxN1 -x(TTT)及TiB2 -TiC -SiC(TTS)的高温蠕变性能和高温氧化行为 .考察在恒定载荷不同温度下 ,材料挠度随时间的变化 .探讨了其高温失效机理 ,并给出了材料抗三点弯曲高温蠕变方程 -挠度 /时间方程 .结果表明 ,含钛复相陶瓷TT ,TTT及TTS在 110 0℃时均出现较大的蠕变 .因此 ,上述 3种材料不宜在 110 0℃及以上的温度下使用 .指出失效的原因之一是TiB2 陶瓷在 80 0℃时的高温氧化及 110 0℃时的高温热分解 .
High-temperature creep behavior and oxidation of ceramics containing titaniferous compound, TiB2-TiC (TT), TiB2-TiCxN1-x (TTT) and TiB2-TiC-SiC (TTS), were investigated. A calculating equation of high-temperature creep for three-point bending test was presented. The relationship between the deflection and the time was given. The results indicate that a rather large creep appears in the diphase ceramics containing titaniferous compound, TT, TTT and TTS, under the load of 156 MPa at 1100°C. It is pointed out that the possible reasons for the creep failure are mainly the high-temperature oxidation at 800^DDGC and the thermal decomposition at 1100°.
出处
《硅酸盐学报》
EI
CAS
CSCD
北大核心
2002年第3期300-304,共5页
Journal of The Chinese Ceramic Society
基金
国家杰出青年基金资助项目 (5 0 12 5 2 0 4)
国家自然科学基金资助项目 (5 990 2 0 0 7)
北京市自然科学基金资助项目(2 0 0 2 0 19) .