A Laval-type supersonic gas atomizer was designed for low-pressure gas atomization of molten metals. The principal design ob-jectives were to produce small-particle uniform powders at lower operating pressures by improving the gas inlet and outlet structures and op-timizing structural parameters. A computational fluid flow model was developed to study the flow field characteristics of the designed atom-izer. Simulation results show that the maximum gas velocity in the atomization zone can reach 440 m＆#183;s-1;this value is independent of the atomization gas pressure P0 when P0〉0.7 MPa. When P0=1.1 MPa, the aspiration pressure at the tip of the delivery tube reaches a mini-mum, indicating that the atomizer can attain the best atomization efficiency at a relatively low atomization pressure. In addition, atomization experiments with pure tin at P0=1.0 MPa and with 7055Al alloy at P0=0.8 and 0.4 MPa were conducted to evaluate the atomization capa-bility of the designed atomizer. Nearly spherical powders were obtained with the mass median diameters of 28.6, 43.4, and 63.5μm, respec-tively. Compared with commonly used atomizers, the designed Laval-type atomizer has a better low-pressure gas atomization capability.
A Laval-type supersonic gas atomizer was designed for low-pressure gas atomization of molten metals. The principal design ob-jectives were to produce small-particle uniform powders at lower operating pressures by improving the gas inlet and outlet structures and op-timizing structural parameters. A computational fluid flow model was developed to study the flow field characteristics of the designed atom-izer. Simulation results show that the maximum gas velocity in the atomization zone can reach 440 m＆#183;s-1;this value is independent of the atomization gas pressure P0 when P0〉0.7 MPa. When P0=1.1 MPa, the aspiration pressure at the tip of the delivery tube reaches a mini-mum, indicating that the atomizer can attain the best atomization efficiency at a relatively low atomization pressure. In addition, atomization experiments with pure tin at P0=1.0 MPa and with 7055Al alloy at P0=0.8 and 0.4 MPa were conducted to evaluate the atomization capa-bility of the designed atomizer. Nearly spherical powders were obtained with the mass median diameters of 28.6, 43.4, and 63.5μm, respec-tively. Compared with commonly used atomizers, the designed Laval-type atomizer has a better low-pressure gas atomization capability.