摘要
The double hard magnetic phase magnets with nominal compositions of Nd30–xDyxFe69B1（x=2, and 4）（wt.%） were prepared. The magnetic properties of the magnets were measured with a NIM-2000H hysteresigraph. The crystalline structures of the magnets were identified by X-ray diffraction（XRD）. The Rietveld refinement was carried out using the FULLPROF software. The scanning electron microscopy（SEM） and transmission electron microscopy（TEM） analyses were carried out in order to investigate the microstructure of the magnets. It showed that the magnets consisted mainly of Nd2Fe14 B phase, and some Nd-rich phase. Two types of matrix-phase grains in dark grey and light grey were found in the magnets with x=2 and 4. The Dy content was obviously different in the two types of grains, which proved that the double hard magnetic phases（Dy-rich and Dy-lean phases） coexisted in the magnet. It revealed that the Nd-rich phases in junction regions had fcc structure, with the unit cell parameter of about 0.52–0.56 nm. The weak superlattice spots were found in the SAD patterns of the junction Nd-rich phases with large scale. The double hard magnetic phase structure seemed to improve the magnetic properties of NdFeB magnets with high coercivity, while decrease the consumption of Dy element, compared with the single alloy magnet.
The double hard magnetic phase magnets with nominal compositions of Nd30–xDyxFe69B1（x=2, and 4）（wt.%） were prepared. The magnetic properties of the magnets were measured with a NIM-2000H hysteresigraph. The crystalline structures of the magnets were identified by X-ray diffraction（XRD）. The Rietveld refinement was carried out using the FULLPROF software. The scanning electron microscopy（SEM） and transmission electron microscopy（TEM） analyses were carried out in order to investigate the microstructure of the magnets. It showed that the magnets consisted mainly of Nd2Fe14 B phase, and some Nd-rich phase. Two types of matrix-phase grains in dark grey and light grey were found in the magnets with x=2 and 4. The Dy content was obviously different in the two types of grains, which proved that the double hard magnetic phases（Dy-rich and Dy-lean phases） coexisted in the magnet. It revealed that the Nd-rich phases in junction regions had fcc structure, with the unit cell parameter of about 0.52–0.56 nm. The weak superlattice spots were found in the SAD patterns of the junction Nd-rich phases with large scale. The double hard magnetic phase structure seemed to improve the magnetic properties of NdFeB magnets with high coercivity, while decrease the consumption of Dy element, compared with the single alloy magnet.
基金
Project supported by the National Basic Research Program of China(2014CB643701,2010CB934601)
the National Science and Technology Support Program of China(2012BAE02B01)
the National Natural Science Foundation of China(51331003,51271060,51171049)
the National Key Technology R&D Program(2012BAE02B01)