The effects of heat treatments on the phase transformation behavior of Ti49Ni49.5Fe1V0.5and Ti48Ni48.5Fe1V2.5 alloys were investigated. The results indicate that the alloys subjected to different heat treatments have B2 structure at room temperature. All the specimens exhibit a twostage B2 → R → B19r martensitic transformation on cooling, but a B19’ → B2 one-stage reverse martensitic transformation on heating except aged A1 alloy, which undergoes an abnormal two-stage transformation upon heating. The phase transformation temperatures are affected by heat treatments and V content, which can be attributed to the variation of the second-phase particles content in the matrix.
The effects of heat treatments on the phase transformation behavior of Ti49Ni49.5Fe1V0.5and Ti48Ni48.5Fe1V2.5 alloys were investigated. The results indicate that the alloys subjected to different heat treatments have B2 structure at room temperature. All the specimens exhibit a twostage B2 → R → B19r martensitic transformation on cooling, but a B19’ → B2 one-stage reverse martensitic transformation on heating except aged A1 alloy, which undergoes an abnormal two-stage transformation upon heating. The phase transformation temperatures are affected by heat treatments and V content, which can be attributed to the variation of the second-phase particles content in the matrix.
基金
financially supported by the Industry,Education and Research Projects of the China Aviation Industrial(No.cxy2012BH04)