摘要
在铜铝镍合金的基础上,通过添加锰和硼元素制备了新型五元铜铝镍形状记忆合金,并对其在不同温度下进行淬火处理,研究了淬火温度对组织、相结构、硬度、电阻率以及相变温度的影响。结果表明:不同温度淬火后合金的组织均为M18R结构的马氏体;随着淬火温度的升高,马氏体板条变得更宽、更平直,合金的硬度变化不大,合金的电阻率先下降后升高,并在700℃达到最低值,合金的相变温度先下降后升高,并且800℃淬火后达到最高。
A new CuA1Ni shape memory alloy was prepared by adding Mn and B elements based on CuA1Ni alloy, and then quenched at different temperatures to study the effects of quenching temperature on the microstructure, phase structure, hardness, resistivity as well as phase transition temperature. The results show that the microstructure of alloy after quenching at different temperatures was martensite with structure of M18R. As the temperature increased, the martensite laths became significant difference; the resistivity of as-quenched alloy value at 700 ℃ ; the transition temperature decreased first, wider and straighter; hut the hardness of alloy had no decreased first, then increased, and reached minimum then increased, and reached maximum value at 800℃.
出处
《机械工程材料》
CAS
CSCD
北大核心
2014年第2期28-31,共4页
Materials For Mechanical Engineering
关键词
铜铝镍形状记忆合金
淬火温度
相变温度
硬度
电阻率
CuA1Ni shape memory alloy
quenching temperature
phase transition temperature
hardness
resistivity