摘要
Zeolite ZSM 5 membrane, whose permeance was up to 10 -6 mol/(m 2·s·Pa) and a magnitude higher than that of other groups, was prepared on α Al 2O 3 support by multi in situ hydrothermal treatments, using optimized sol prescription and cheap n butane as the structure directing agent. The membrane was characterized by means of XRD, SEM and single gas permeances measurements, which showed that it was dense and integral without large intercrystal pores and cracks. The permeance of H 2, N 2, C 3H 8 and n C 4H 10 was up to 2.35×10 -6 , 1.0×10 -6 , 1.13×10 -7 and 4.9×10 -8 mol/(m 2·s·Pa), respectively. Ideal selectivity of H 2/N 2, H 2/C 3H 8 and H 2/ n C 4H 10 was 2.45, 20.8 and 48, respectively. [WT5HZ]
Zeolite ZSM 5 membrane, whose permeance was up to 10 -6 mol/(m 2·s·Pa) and a magnitude higher than that of other groups, was prepared on α Al 2O 3 support by multi in situ hydrothermal treatments, using optimized sol prescription and cheap n butane as the structure directing agent. The membrane was characterized by means of XRD, SEM and single gas permeances measurements, which showed that it was dense and integral without large intercrystal pores and cracks. The permeance of H 2, N 2, C 3H 8 and n C 4H 10 was up to 2.35×10 -6 , 1.0×10 -6 , 1.13×10 -7 and 4.9×10 -8 mol/(m 2·s·Pa), respectively. Ideal selectivity of H 2/N 2, H 2/C 3H 8 and H 2/ n C 4H 10 was 2.45, 20.8 and 48, respectively. [WT5HZ]
出处
《高等学校化学学报》
SCIE
EI
CAS
CSCD
北大核心
2000年第12期1812-1814,共3页
Chemical Journal of Chinese Universities
基金
中国石油化学工业总公司"九五"重大攻关项目 !(批准号 :4970 16)资助
关键词
水热晶化
ZSM-5沸石膜
渗透率
选择性
合成
Hydrothermal crytallization
Zeolite ZSM 5 membrane
Permeance
Selectivity