炭/炭复合材料ZrC涂层的制备及显微组织结构 被引量:4

Preparation and microstructure of ZrC coatings for C/C composites
在线阅读 下载PDF
导出
摘要 通过冷态输送ZrCl4粉末,利用低压化学气相沉积法在C/C复合材料表面制备ZrC涂层。采用X射线衍射和扫描电镜研究沉积温度和沉积位置对ZrC涂层物相成分和微观形貌的影响。结果表明:在1 400~1 600℃时,沉积涂层物相均为单一的ZrC。ZrC晶粒择优取向随沉积温度的升高而发生变化;在1 400和1 500℃时,ZrC晶粒择优取向面为(200);1 600℃时,晶粒择优取向面转变为(220)和(200),且择优不明显;随着沉积温度的进一步升高,涂层晶粒尺寸明显增大,涂层表面ZrC颗粒由球形逐渐转变为金字塔形多面体。在1 400~1 600℃沉积时,反应器的100~230mm沉积区间内可以得到成分单一、择优取向一致、表面形貌相同的ZrC涂层。 ZrC coatings were deposited on C/C composites by low pressure chemical vapor deposition(LPCVD) at different temperatures,and the ZrCl 4 powders were transported in solid state.X-ray diffractometry and scan electron microscopy were employed to investigate the effects of deposition temperature and position on the phases and surface morphologies of ZrC coatings.The results show that the coatings are composed of cubic ZrC in the temperature range from 1 400 ℃ to 1 600 ℃.The preferred orientation of the ZrC coatings varies with the growth temperature increasing. At 1 400 and 1 500 ℃,the preferred orientation of the ZrC coating is(200),but it changes to(220) and(200) at 1 600 ℃.As temperature increasing,the grain size increases and the shape of the grains changes from spherical to tetrahedral pyramid.Within the temperature range from1 400 ℃ to 1 600 ℃,the ZrC coatings with uniform phase,orientation and surface morphology are deposited in the reactor scale from-100 mm to-230 mm.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2012年第11期3081-3087,共7页 The Chinese Journal of Nonferrous Metals
基金 国家基础研究发展计划资助项目(2011CB605805) 湖南省研究生创新基金资助项目(CX2009B033)
关键词 ZrC涂层 低压化学气相沉积 相组成 显微组织 均匀性 ZrC coating low pressure chemical vapor deposition phase composition microstructure homogeneity
  • 相关文献

参考文献18

  • 1FITZER E. Future of carbon-carbon composites[J]. Carbon, 1987, 25(2):163-190.
  • 2SMEACETTO F, SALVO M, FERRARIS M. Oxidation protective multilayer coatings for carbon-carbon composites[J]. Carbon, 2002, 40: 583-587.
  • 3WUNDER V, POPOVSKA N, WEGNER A, EMIG G, AMOLD W. Multilayer coatings on CFC composites for high-temperature applications[J]. Surface and Coating Technology, 1998, 100/101: 329-332.
  • 4付前刚,薛晖,李贺军,李丸智,史小红,赵华.多涂层炭/炭复合材料抗1500℃燃气冲刷性能的研究(英文)[J].新型炭材料,2010,25(4):279-284. 被引量:8
  • 5王雅雷,熊翔,李国栋,肖鹏,陈招科.新型C/C-TaC复合材料的微观结构及其力学性能[J].中国有色金属学报,2008,18(4):608-613. 被引量:6
  • 6LI Guo-dong, XIONG Xiang, HUANG Ke-long. Ablation mechanism of TaC coating fabricated by chemical vapor deposition on carbon/carbon composites[J]. Transactions of Nonferrous Metals Society of China, 2009(s3), 19: s689-s695.
  • 7LEE Y J, JOO H J. Ablation characteristics of carbon fiber reinforced carbon (CFRC) composites in the presence of silicon carbide (SIC) coating[J]. Surface and Coating Technology 2004, 180/181: 286-289.
  • 8WANG Yong-jie, LI He-jun, FU Qian-gang, WU Heng, YAO Dong-jia, WEI Bing-bo. Ablative property of HfC-based multilayer coating for C/C composites under oxy-acetylene torch[J]. Applied Surface Science, 2011,257: 4760-4763.
  • 9JAMES R S, JAMES E S. Ceramic coating for carbon-carbon composites[J]. Ceram Bull, 1988, 67(2): 369-374.
  • 10SAYIR A. Carbon fiber reinforced hafnium carbide composite[J]. Journal of Materials Science, 2004, 39: 5995-6003.

二级参考文献53

共引文献32

同被引文献57

引证文献4

二级引证文献34

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部