The homogeneous liquid was separated into two phases, （Fe, Co）-rich LI and Cu-rich L2, once the melt was undercooled below a liquid-phase separation temperature Tsep. If the duration from Tsep to Tsl （solidification temperature of LI phase）, termed the liquid-phase separation interval Δt, exceeded a critical value, an eggtype structure was observed. By utilizing differential thermal analyses （DTA）, the solidification process of the undercooled Fe-Co-Cu alloys was studied. Additionally, an immiscible boundary was obtained, which was a convex parabola with a symmetrical axis of XCu=0.52. Depending on the relative amounts of LI and L2, the minor phase was nucleated firstly to form liquid droplets and separated from the original liquids at the beginning of liquid-phase separation.
The homogeneous liquid was separated into two phases, （Fe, Co）-rich LI and Cu-rich L2, once the melt was undercooled below a liquid-phase separation temperature Tsep. If the duration from Tsep to Tsl （solidification temperature of LI phase）, termed the liquid-phase separation interval Δt, exceeded a critical value, an eggtype structure was observed. By utilizing differential thermal analyses （DTA）, the solidification process of the undercooled Fe-Co-Cu alloys was studied. Additionally, an immiscible boundary was obtained, which was a convex parabola with a symmetrical axis of XCu=0.52. Depending on the relative amounts of LI and L2, the minor phase was nucleated firstly to form liquid droplets and separated from the original liquids at the beginning of liquid-phase separation.
基金
supported by the Natural Science Foundation of China (Grant No.50771084)
the Natural Science Foundation of the Education Department of Jiangsu province,China (Grant No.09KJB430004)