N08810耐蚀合金200mm厚连铸板坯纵向裂纹形成机理的分析 被引量:6

An Analysis on Forming Mechanism of Longitudinal Crack of N08810 Corrosion Resistant Alloy 200 mm Thickness Casting Slab
在线阅读 下载PDF
导出
摘要 通过光学、扫描电子显微镜、能谱仪和G1eeble-3800热模拟试验机对1流立式连铸机生产的UNSN08810合金(/%:0.06C、0.45Si、0.92Mn、0.016P、0.001S、30.15Ni、19.80Cr、47.81Fe、0.33Ti、0.23Al、0.014 0N)200 mm1×1 300 mm连铸坯的纵向裂纹进行了分析。结果表明,纵向裂纹沿粗大的柱状晶晶界向铸坯内部扩展、裂纹深度为18~20 mm。高温塑性试验得出,当温度≥1100℃时合金的断面收缩率急剧下降。分析表明,凝固初期柱状晶之间连接比较薄弱,易在晶界处开裂,加上晶界处脆性相TiC的析出,造成应力集中,并使裂纹更容易延晶界扩散,最终形成纵向裂纹。 An analysis on longitudinal crack of 200 mm×1 300 mm casting slab of UNS N08810 alloy(/%:0.06C, 0.45Si,0.92Mn,0.016P,0.001S,30.15Ni,19.80Cr,47.81Fe,0.33Ti,0.23Al,0.0140N) produced by one-strand vertical continuous casting machine has been carried out by optical,scanning electron microscope,energy dispersive spectrometer and Gleeble-3800 thermal simulation machine.Results show that the longitudinal crack extends along grain boundary of coarse columnar crystal towards inner casting slab,the depth of crack is 18~20 mm.Test of high temperature plasticity of allov obtains that as temperature≥1100℃the reduction of area of alloy dramatically decreases.And the analysis indicates that at early period of solidification the connection between columnar dendrites is weak,the boundary of columnar crystal easily cracks,in addition the brittle phase TiC deposits at grain boundary lead to stress concentration,the crack easily extends along grain boundary to form the longitudinal crack finally.
出处 《特殊钢》 北大核心 2012年第3期61-64,共4页 Special Steel
关键词 N08810耐蚀合金 连铸板坯 纵向裂纹 形成机理 分析 N08810 Corrosion Resistant Alloy Casting Slab Longitudinal Crack Forming Mechanism Analysis
  • 相关文献

参考文献13

  • 1Dehmolaei R, Shamanian M. Microstructural Changes and Mechanical Properties of Incoloy 800 After 15 Years Service. Materials Character- ization ,2009,60( 3 ) :246.
  • 2Shailesh J P. A Century of Discoveries, Inventors, and New Nickel Al- loys. The Journal of the Minerals ,Metal & Materials Society,2006,58 (9):18.
  • 3张兴中,那贤昭,王忠英,刘爱强,干勇.圆坯方坯凝固定律的导出和验证[J].金属学报,2004,40(3):281-284. 被引量:18
  • 4蔡开科.连铸坯表面裂纹的控制[J].鞍钢技术,2004(3):1-8. 被引量:107
  • 5Brimacombe J, Sorimachi K. Crack Formation in the Continuous Cast- ing of Steel. Metallurgical and Materials Transactions, 1977,8 (2) : 489.
  • 6Shin H J,Kim S H,Thomas B G,et al. Measurement and Prediction of Lubrication, Powder Consumption, and Oscillation Mark Profiles in Ul- tra-low Carbon Steel Slabs. ISIJ International ,2006,46 (11 ) :1635.
  • 7Kanbe Y, Ishii T, Todoroki H, et al. Prevention of Longitudinal Cracks in a Continuously Cast Slab of Fe-Cr-Ni Superalloy Containing A1 and Ti. International ,loumal of Cast Metals Research ,2009,22( 1-4 ) :143.
  • 8陈国胜,金鑫,周奠华,王世普,谢伟,王林涛.硼含量对镍基合金GH4049晶界析出相和高温性能的影响[J].金属学报,2005,41(6):622-626. 被引量:23
  • 9郭建亭 张金岩 黄荣芳 等.GH135合金的晶界沉淀相与冲击韧性和缺口敏感性的关系[J].金属学报,1985,21(6):413-413.
  • 10乔雪璎,王延庆,蒙肇斌,吕俊英.碳含量对GH4199合金拉伸、持久性能及组织的影响[J].材料与冶金学报,2004,3(1):62-66. 被引量:11

二级参考文献26

  • 1吕俊英,张玉锁,崔彤,童开峰,杨洪才,王延庆,蒙肇斌.GH4199合金的组织稳定性[J].钢铁研究学报,2003,15(z1):135-138. 被引量:1
  • 2张红斌主编.镍基高温合金译文集[C].钢铁研究总院、冶金工业部、长城钢厂等联合出版,1983..
  • 3高温合金金相图谱编写组编著.高温合金金相图谱[M].北京:冶金工业出版社,1977..
  • 4李玉清 刘锦岩.高温合金间隙相[M].北京:冶金工业出版社,1990..
  • 5Adams M C. Liquid Metals and Solidification, Cleveland Ohio: American Society for Metals, 1958:187
  • 6Okamoto T. Casting, 1977; 49(10): 624
  • 7Mizikar E A. Trans Metall Soc AIME, 1967; 239:1747
  • 8Yang H L, Zhao L G, Zhang X Z, Deng K W, Gan Y.Metall Mater Trans, 1998; 29B: 1345
  • 9GautieJ J R, Morillon Y, Dumont-Fillon J. JISI, 1970;208:1053
  • 10Franzoni U, Marchetti F, Sturlese S. Scr Metall, 1985; 19:511.

共引文献181

同被引文献47

引证文献6

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部