HDPE与PPR全切痕拉伸断裂过程银纹性能测试 被引量:1

Measurement of Craze Behavior in CDNT Fracture Procedure for HDPE and PPR
在线阅读 下载PDF
导出
摘要 通过对高密度聚乙烯(HDPE)和无规共聚聚丙烯(PPR)进行不同拉伸速率的全切痕拉伸测试,考察了两种材料在近似于平面应变条件的拉伸断裂性能。对其全切痕拉伸过程应力-位移曲线、位移-屈服应力曲线分析:HDPE和PPR的屈服应力均随着拉伸速率的增加而增大;在较高拉伸速率时,HDPE全切痕拉伸断裂可认为是由常临界位移控制的银纹断裂,PPR的全切痕拉伸断裂过程几乎无恒定的常拉伸位移。通过显微镜显示的断裂形貌观察揭示了沿拉伸方向上HDPE有微纤空穴产生;在全切痕拉伸断裂过程中,PPR的银纹化易于发生在非晶区的片晶间,银纹微纤可产生在任意方向上。 High density polyethylene (HDPE) and random polypropylene copolymerized (PPR) were tested by using the circumferentially deep notched tensile (CDNT) specimens with different tensile rates and the properties of tensile fracture of two kinds of materials were analyzed under approximate plane strain condi- tion. Based on the analysis of curves of the stress-extension and the extension-yield stress, the results showed that the yield stress of HDPE and PPR increased with an increase of the tensile rate ; at higher tensile rate the tensile fracture of CDNT for HDPE was craze fracture which was controlled by the constant critical extension while these were almost not a constant critical extension for PPR in the CDNT fracture procedure. The micro- photography of fracture surface of HDPE indicated fibril and void were produced at the tensile direction ; Crazing was easily produced between lamellar crystals in the amorphous region at the CDNT fracture procedure and craze fibrils can be produced at every direction for PPR.
出处 《塑料工业》 CAS CSCD 北大核心 2012年第4期78-81,105,共5页 China Plastics Industry
基金 西华大学研究生创新基金项目(YCJJ201153)西华大学重点科研基金项目(Z0720106) 四川省科技厅应用基础研究重点项目(08JY0109)
关键词 拉伸断裂 屈服应力 银纹 临界应变 微纤 Tensile Fracture Yield Stress Craze Critical Strain Fibril
  • 相关文献

参考文献13

  • 1DEBLIECK R A C, VAN BEEK D J M, REMERIE K, et al. Failure mechanisms in polyolefines: The role of crazing, shear yielding and the entanglement network [ J ]. Polymer, 2011, 52 (14): 2979 -2990.
  • 2DUAN D M, WILLIAMS J G. Craze testing for tough polyethylene [J]. J Mater Sci, 1998, 33 (3) : 625-638.
  • 3PANDYA K C, WILLIAMS J G. Measurement of cohesive zone parameters in tough polyethylene [ J]. Polym Eng Sci, 2000, 40 (8) : 1765 -1776.
  • 4IVANKOVIC A, PANDYA K C, WILLIAMS J G. Crack growth predictions in polyethylene using measured traction- separation curves [J]. Eng Fract Meeh, 2004, 71 (4-6) : 657 - 668.
  • 5LEEVERS P S. Interpreting instrumented three point bendfracture tests on craze forming polymers [ J ]. Plast Rubber Compos, 2000, 29 (9), 453-459.
  • 6刘松林,沈静姝.分子量对聚丙烯银纹形态的影响[J].高分子学报,1993,3(3):361-365. 被引量:7
  • 7SUGIMOTO M, ISHIKAWA M, HATADA K. Toughness of polypropylene [ J ]. Polymer, 1995, 36 (19): 3675 - 3682.
  • 8刘文娴,张平,颜志军.改性聚丙烯材料裂尖银纹损伤研究[J].材料科学与工程学报,2003,21(4):531-534. 被引量:5
  • 9孙载坚.塑科增韧[M].北京:化学工业出版杜,1982:156.
  • 10李历生 聂宗武 刘忠纯.聚乙烯球晶在单向拉伸下的形变Ⅱ.高分子通讯,1979,(5):291-297.

二级参考文献14

  • 1Knauss WG. [J]. Eng Mater Tech, 1993,115:262 ~ 267.
  • 2Yang Tingqing ( 杨挺青 ), An Qunli, Luo Wenbo. [ J ]. Polym Eng Sci, 2001,41(7):1171 ~ 1176.
  • 3Jie M, Tang CY, Li YP et al. [J].Theor Appl Fracture Mech,1998,28:165 - 174.
  • 4Tang CY, Peng LH, Li CC, et al. [J]. Polymer testing, 2001,20:241 ~ 251.
  • 5Michler G H, et al. [J]. Phil Mag, 1999,A79(1):167 ~ 178.
  • 6Kausch H H (ed). [ M ]. Advances in polymer science, 91/92,Crazing in polymers, Belin : Springer-Verlag, 1991.
  • 7Brown N, Lu X. [ J ]. Polymer, 1995,36 (3) : 543 ~ 548.
  • 8Yang A C M,Macromolecules,1986年,19卷,2010页
  • 9Yang A C M,Macromolecules,1986年,19卷,2020页
  • 10赵得禄,高分子通讯,1981年,3期,385页

共引文献28

同被引文献5

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部