研究了Ti600钛合金在700-1000℃范围内的氧化行为。结果表明,Ti600的100 h氧化动力学近似遵循抛物线-直线规律,氧化激活能为224 kJ·mol^(-1)。Ti600试样在700℃氧化100 h后其表面形成了致密的氧化皮,而在高于700℃氧化100 h后氧化皮出现多层结构并开始剥落,氧化皮主要由金红石型TiO_2和α-Al_2O_3组成。Ti600试样在700-1000℃氧化后,氧化皮下方的氧扩散区(ODZ)形成了多层结构,随着氧化温度的升高和氧化时间的延长,ODZ区的厚度和氧在ODZ的溶解度随之提高。
Oxidation behavior of titanium alloy Ti600 at 700-1000℃was investigated.Results showed that the oxidation kinetics of the Ti600 alloy followed the parabolic-linear law and the activation energy of oxidation was 224 kJ·mol^（-1） under the condition of oxidation at 700-1000℃for 100 h. Dense oxide scales formed on the sample surface at 700℃for 100 h,while oxide scales with multilayer microstructure formed at the temperature above 700℃began spalling.Oxide scales mainly compose of rutile andα-Al_2O_3.Oxidation diffusion zone（ODZ） beneath oxide scale has sub-layer microstructure formed at 700-1000℃.The thickness of ODZ sub-layers and oxygen solubility in ODZ increased with the increase of oxidation temperature and prolonging of the oxidation time.
出处
《材料研究学报》
EI
CAS
CSCD
北大核心
2011年第3期295-302,共8页
Chinese Journal of Materials Research
基金
国家科技支撑计划2007BAE07B0X
安徽工业大学优秀创新团队基金资助项目~~
关键词
金属材料
TI600钛合金
氧化
分层结构
metallic material
Ti600 titanium alloy
oxidation
multilayer structure