摘要
通过沉淀法制备碳酸铝铵超细粉体均匀包裹的氧化铝粉体,煅烧后,继令其与纳米二氧化硅按一定比例球磨混合,预烧,添加适当的粘结剂和造孔剂,再经捏合、陈腐、挤出成型、烘坯、烧结,制备膜支撑体。结果表明,二氧化硅加入量为12%(质量分数)、1550℃烧结所得的膜支撑体综合性能较好:纯水通量为22.2m3/(m2·h);爆破压力为3.40MPa,开孔率为40.21%;经10%(质量分数)H2SO4或5%(质量分数)NaOH于100℃下浸渍36h后,爆破压力仍分别为2.67和2.89MPa,表明它还具有良好的耐酸碱性能。
Prepared by precipitation method with aluminium nitrate and ammonium acid carbonate,after calcining,superfine powder coated alumina was ball-mill mixed with nano-silica in a certain proportion,then pre-sintered,an appropriate amount binder and pore-forming agent were added.After kneading,aging、extrusion molding and drying,the membrane supports were temperature-programming sintered to certain temperature and held for 2h.It is shown that support body with 12wt% SiO2 and sintered at 1550℃ has much better comprehensive functions： water flux is 22.21m3/（m2·h）,the bursting strength is 3.40MPa,and open porosity is 40.21%.After dipping in 10wt% H2SO4 or 5wt% NaOH for 36h at 100℃ respectively,the membrane support still has a bursting high up to 2.67MPa and 2.89MPa,it indicates that the acid resistance and alkaline resistance property of the membrane support is excellent.
出处
《功能材料》
EI
CAS
CSCD
北大核心
2011年第3期425-428,431,共5页
Journal of Functional Materials
关键词
沉淀法
多孔陶瓷膜支撑体
挤出成型
precipitation method
porous ceramic membrane support
extrusion molding