Ti-10Cr合金析出相对硬度的影响 被引量:1

Influence of precipitated phase on hardness of Ti-10Cr alloy
在线阅读 下载PDF
导出
摘要 测试Ti-10Cr合金经900℃固溶及400~700℃时效后的维氏硬度,采用XRD和TEM分析析出相的成分及形貌,研究硬度、析出相特征与热处理制度之间的关系。结果表明:经900℃固溶空冷后,析出相为细小、弥散的等轴ω相和少量α相,合金硬度达到HV560;经400℃时效后,ω相和α相长大,合金硬度值稍有下降;经500℃时效后,ω相消失,α相长大为片状,合金硬度明显降低;当继续升高时效温度时,片状α相会进一步长大,合金的硬度缓慢降低。 The Vickers-hardness of Ti-10Cr alloy was tested after being solution treated at 900 ℃ as well as following by aging treatment at 400-700 ℃. The precipitated phases and their morphologies during solution and aging were analyzed by XRD and TEM. Furthermore, the relationships among hardness, phase precipitation and heat treatment were discussed. The results indicate that the fine dispersion isothermal ω phase and few a phase form in the metastable beta matrix after solution treatment at 900 ℃ following by air cold. Under this condition, the hardness reaches HV560. co phase and a phase grow after aging at 400 ℃, and the hardness shows a little decrease, ω phase is decomposed and a phase becomes lamella after aging at 500 ℃, and the hardness value of the alloy deceases remarkable. After that, with the increase of aging temperature, the hardness decreases slowly due to the a phase growth.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2010年第B10期1-5,共5页 The Chinese Journal of Nonferrous Metals
基金 国家重点基础研究发展计划资助项目(2007CB613805) 国家科技支撑计划资助项目(2007BAE07B03)
关键词 Ti-10Cr合金 析出相 相形貌 维氏硬度 Ti-10Cr alloy precipitated phase morphology Viekers-hardness
  • 相关文献

参考文献19

  • 1National Association of Corrosion Engineers (USA). Fundamentals of Corrosion and protection techniques[M]. ZHU Ri-zhang, et al, transl. Beijing: Metallurgical Industry Press,1987: 307.
  • 2LIVINGSTON J D. Laves-phase superalloys?[J]. Physica Status Solidi(a), 1992, 131 (2): 415-423.
  • 3TAKEMOTO S, HATTORI M, YOSHINARI M, KAWADA, ASAMI K, ODA Y. Corrosion behavior and surface characterization of Ti-20Cr alloy in a solution containing fluoride[J]. Dental Materials Journal, 2004, 23: 379-386.
  • 4肖平安,曲选辉,雷长明,祝宝军,秦明礼,敖晖,黄培云.High temperature oxidation behaviors of Ti-Cr alloys with Laves phase TiCr_2[J].中国有色金属学会会刊:英文版,2002,12(2):200-203. 被引量:2
  • 5KOIKE M, OKABE T, ITOH M, OKUNO O, KIMURA K, TAKEDA O, OKABE T, OKABE T H. Evaluation of Ti-Cr-Cu alloys for dental applications[J]. Journal Materials Engineering and Performance, 2005, 14(6): 778-783.
  • 6HSU H C, WU S C, CHIANG T Y, HOW F. Structure and grindability of dental Ti-Cr alloys[J]. Journal Alloys and Compounds, 2009, 476(1/2): 817-825.
  • 7HOW F, CHIANG T Y, WU S C, HSU H C. Evaluation of low-fusing porcelain bonded to dental cast Ti-Cr alloys[J]. Journal Alloys and Compounds, 2009, 474: 505-509.
  • 8CHEN K C, ALLEN S M, LIVINGSTON J D. Factors affecting the room-temperature mechanical properties of TiCr2-base Laves phase alloys[J]. Materials Science and Engineering A, 1998, 242(1/2): 162-173.
  • 9BANERJEE R, COLLINS P C, FRASER H L. Phase evolution in laser-deposited titanium-chromium aUoys[J]. Metallurgical and Materials Transactions A, 2002, 33(7): 2129-2138.
  • 10AMIRA S, SANTOS S F, HUOT J. Hydrogen sorption properties of Ti-Cr alloys synthesized by ball milling and cold rolling[J]. Intermetallics, 2010, 18(1): 140-144.

二级参考文献24

  • 1陈异,蒋利军,黄倬,詹锋,秦光荣,尉秀英,苑鹏.低放氢压的Ti-Mn基Laves相贮氢合金[J].稀有金属,2001,25(3):215-218. 被引量:6
  • 2雷力明.[D].Beijing,.
  • 3赵永庆.Rare Metal Materials and Engineering(稀有金属材料与工程)[J],2002,31(2):84-84.
  • 4张廷杰.Rare Metal Materials and Engineering(稀有金属材料与工程)[J],1989,6:76-76.
  • 5[1]Johnson J R. Reaction of hydrogen with the high temperature (C14) form of TiCr2[J]. Less-Common Metals, 1980, 73: 345.
  • 6[2]Johnson JR, Reilly JJ, Reidinger F, et al. On the existence of F.C.C. TiCr1.8H5.3[J]. Less-Common Metals, 1982, 88: 107.
  • 7[3]Cho S W, Akika E, akamara Y N, et al. Hydrogen isotope effect in TiMn0.9V1.1 and TiCr1.5V1.7 alloys [J]. Alloys and Compds, 2000, 297: 253.
  • 8[4]Bououdina M, Enoki H, Akika E. The investigation of the Zr1_ yTiy(Cr1_ xNix)2-H2 system 0.0≤ y≤ 1.0, 0.0≤ x ≤ 1.0phase composition analysis and thermodynamics properties [ J ].Alloys and Compds., 1998, 281: 290.
  • 9[5]Boschung E, Zuttel A, Chartouni D, et al. Hydriding properties of the Zr(Cr0.5Ni0.5)α(3.5≥α≥ 1.75) alloy system [J]. Alloys and Compds., 1998, 274: 294.
  • 10[6]Akika E, Iba H. Hydrogen absorption by Laves phase related BCC solid solution [J]. Intermetallics, 1998, 6: 461.

共引文献115

同被引文献14

  • 1刘生发,黄尚宇,徐萍.Ce对AZ91镁合金铸态组织细化的影响[J].金属学报,2006,42(4):443-448. 被引量:59
  • 2李萧,刘江文,罗承萍.铸造ZC62镁合金的时效行为[J].金属学报,2006,42(7):733-738. 被引量:37
  • 3BUHA J. Natural aging Mg-Zn-(Cu) alloys[J]. Metallurgical and Materials Transactions A, 2008, 39A(9) : 2259- 2273.
  • 4BUHA J. Mechanical properties of naturally aged Mg-Zn-Cu-Mn alloy[J].Materials Science and Engineering A, 2008,489(1): 127 -137.
  • 5ZHU H M,SHA G,LIU J W,et al. Mierostructure and mechani- cal properties of Mg-6Zn-xCu-0. 6Zr (wt%) alloys[J]. Journal of Alloys and Compounds, 2011,509(8) : 3526-3531.
  • 6TAMURA YOUSUKE, KONO NORIO, MOTEGI TETSUI- CHI. Grain refining mechanism and casting structure of Mg-Zr alloy[J]. Journal of Japan Institute of Light Metals, 1998,48 (4) :185-189.
  • 7MAKOTO T,SUZUKI T,FUKUI I, et al. Effect of Ti or Ti-B on grain size and meehanieal properties of A1-7% Si-0. 3% Mg casting alloy[J].Journal of Japan Institute of Light Metals, 1979,29(10) ,437-444.
  • 8SASAKI H,ADACHI M,SATO S,et al. Effect of solidified mi- crostructures on mechanical properties of AZ91 magnesium alloy[J].Journal of Japan Institute of Light Metals, 1997,47 (3) : 133 -138.
  • 9HATANI T, TAMURA Y, YANO E, et al. Grain refining mech- anism of high-purity Mg-9A1 alloy ingot and influence of Fe or Mn addition on cast grain size[J]. Journal of Japan Institute of Light Metals,2001,51(8) :403-408.
  • 10TAMURA Y, KONO N, MOTEGI T, et al. Grain refining mechanism and casting of Mg-Zr alloy[J]. Journal of Japan Insti- tute of Light Metals,1998,48(4):79-83.

引证文献1

二级引证文献6

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部