研究了Zn-P合金电镀液组成及工艺条件对镀层含磷量的影响,在最佳工艺参数条件下,可得到磷的质量分数为0.1%左右的Zn-P合金镀层。对镀液、镀层性能进行了测试,实验证明经银白色钝化后的Zn-P合金镀层的耐蚀性能是纯锌镀层的2倍以上。
Influence of electroplating solution ingredients and technological condition on phosphorus content of Zn-P al-loy deposits was studied, and the properties of electroplating solution and coat were studied too. Under the opti-mum condition , the Zn-P alloy electroplating coat with P content about 1% was obtained. The anticorrosion of the electroplating deposit under silvery white passivation was two times as high as that of pure zinc deposit.