随着浓缩倍数的不断上升,循环水中氯离子的增加引起人们对不锈钢设备腐蚀的关注。针对循环水中氯离子的腐蚀进行了实验,实验结果和现场数据说明循环水中硬度在1200mg/L^1500mg/L左右时,氯离子带来的腐蚀是可以控制的。
The corrosion of the stainless steel facility caused by the chloride ions was raised as the concentrate rate rose in the petrochemical plants. Experiments were carried out and the results showed that, the corrosion caused by chloride ions could be controlled when the rigidity of the circulating water was in the range of 1200 mg/L to 1500 mg/L.