Microstructure of solid phase reduction on manganese oxide ore fines containing coal （MOOFCC） is one of important kinetics conditions of influencing microwave heating. On condition thai an atomic molar ratio of ro ： rc in MOOFCC is 1 ： 1.06 as well as a molecular molar ratio of rSiO2： rCaO is 1 ： 1.28, 1 kg of MOOFCC is heated by microwave to reach 1 000-1 300℃ and hold different time respectively. Experiments show that the metal phase takes the iron-based metal compounds containing manganese as the main content. The manganese content of metal phase increases with the xise of temperature. The particle size of the metal phase is within the range from 0. 01 to 0.05 mm. MO2 phase in the stuff is entirely changed into MnO phase and the slag phase is mainly composed of wollastonite and manganese olivine. The stuff reduced is loose and massive as a whole and its porosity is from 30% to 45%. The low softening-melting property and the low density of the stuff impact, to some degree, the solid phase reduction of powder by microwave heating.
Microstructure of solid phase reduction on manganese oxide ore fines containing coal （MOOFCC） is one of important kinetics conditions of influencing microwave heating. On condition thai an atomic molar ratio of ro ： rc in MOOFCC is 1 ： 1.06 as well as a molecular molar ratio of rSiO2： rCaO is 1 ： 1.28, 1 kg of MOOFCC is heated by microwave to reach 1 000-1 300℃ and hold different time respectively. Experiments show that the metal phase takes the iron-based metal compounds containing manganese as the main content. The manganese content of metal phase increases with the xise of temperature. The particle size of the metal phase is within the range from 0. 01 to 0.05 mm. MO2 phase in the stuff is entirely changed into MnO phase and the slag phase is mainly composed of wollastonite and manganese olivine. The stuff reduced is loose and massive as a whole and its porosity is from 30% to 45%. The low softening-melting property and the low density of the stuff impact, to some degree, the solid phase reduction of powder by microwave heating.
基金
Item Sponsored by National Natural Science Foundation of China (50674069)