采用热分析仪、光学显微镜等研究了3104铝合金的铸态和不同工艺均匀化退火后的显微组织,为其制定了合理的均匀化退火工艺,利用扫描电镜及其附件确定了合金均匀化退火后组织中主要化合物的形貌及类型。结果表明:3104铝合金合适的均匀化退火工艺为590℃保温12 h;均匀化退火后,因合金成分的差异,形成了形貌各异、类型不同的金属间化合物,主要有(FeMn)Al6、MnAl6、(Al、Fe、Mn、Si)四元相、Mg2Si相、(Al、Mn、Si)三元相、Al8Mg5、(Al、Mn、Mg、Fe)四元相等。
The microstructure of as-casted and homogenizing annealing with different parameters 3104 aluminum alloy were studied by means of thermal analysis and optical microscope, then homogenization annealing parameters were determined. The morphology and types of main compounds were studied by scanning electron microscope and its accessory. The results show that the reasonable homogenizing annealing parameters was 590 ℃ for 12 h, and various compounds appeared due to the difference of main alloy components after homogenizing annealing which mainly consisting of （FeMn）Al6, MnAl6, （Al, Fe, Mn, Si） quaternary phase, Mg2Si phase, （Al, Mn, Si） ternary phase, A18Mg5, （Al, Mn, Mg, Fe） quaternary phase and so on.
出处
《机械工程材料》
CAS
CSCD
北大核心
2010年第1期9-12,共4页
Materials For Mechanical Engineering
关键词
3104铝合金
均匀化退火
显微组织
3104 aluminum alloy
homogenizing annealing
microstructure