摘要
对用快硬硫铝酸盐水泥制备ＨＰＣＭ的工艺条件进行了试验与研究，证实采用ｗ／ｃ＝０．１６，成型压力４０～５０ＭＰａ，常规养护条件，可以较容易地制得抗压强度为１２０～１４０ＭＰａ的ＨＰＣＭ。
The technique of preparing high performacne cement-based materials(HPCM) from sulphoaluminate cement was studied. The experiment showed that HPCM with 120～140MPa compressive strength could easily be made with W/C=0 16 and under a forming pressure of 40～50MPa and ordinary curing conditions.
出处
《硅酸盐通报》
CAS
CSCD
1998年第4期9-14,共6页
Bulletin of the Chinese Ceramic Society
关键词
水泥基材料
硫铝酸盐
水泥
HPCM
high performance cement-based materials, cement-based materiale, cement, sulphoaluminate cement